Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength		ASTM D256/ISO 179	85 kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	13 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength		ASTM D256/ISO 179	11 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	70 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	11.5 kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ASTM D638/ISO 527	10000 kg/cm²(MPa)[Lb/in²]
Flexural modulus		ASTM D790/ISO 178	8600 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	280 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	3 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric constant		ASTM D150/IEC 60250	3.5
Volume resistivity		ASTM D257/IEC 60093	1E 13 Ω.cm

Physical properties	روش آزمون	نتیجه آزمون
density	ASTM D792/ISO 1183	1360
Shrinkage rate	ASTM D955	0.55 %
melt mass-flow rate	ASTM D1238/ISO 1133	40 （cm3/10min 275℃/5kg ) g/10min
Water absorption rate	ASTM D570/ISO 62	1.5-1.9 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	HDT	ASTM D648/ISO 75	240(1.80MPa) ℃（℉）
melting temperature			260 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.2-0.3 mm/mm.℃