برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 7 g/10min Water absorption rate ASTM D-570 0.15 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ASTM D-790 91 Mpa Impact strength of cantilever beam gap 23°C ASTM D-256 640 J/m Rockwell hardness ASTM D-785 118 elongation Break ASTM D-638 90 % tensile strength Yield点 ASTM D-638 62 Mpa tensile strength Break点 ASTM D-638 56 Mpa Bending modulus ASTM D-790 Mpa MPa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa ASTM D-648 132 °C Vicat softening temperature ASTM D-1525 151 °C Long term use temperature UL 746B 120 °C Hot deformation temperature 0.45MPa ASTM D-648 137 °C Linear coefficient of thermal expansion ASTM E-831 6.8×10 1/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 1.6 mm UL flame retardant rating UL 94 V-0 density ASTM D-792 1.21 Shrinkage rate 3.2mm ASTM D-955 5-7 10 UL flame retardant rating UL 94 V-2 UL flame retardant rating UL 94 3.0 mm
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D-257 1.0×10 Ω.cm Dissipation factor 1MHz ASTM D-150 0.01 Dissipation factor 60Hz ASTM D-150 0.0009 Dielectric constant 60Hz ASTM D-150 3.01 Dielectric constant 1MHz ASTM D-150 2.96