برگه داده فنی مقایسهelastomer شرایط آزمون روش آزمون نتیجه آزمون Permanent compression deformation 200%Strain ASTM D412 8 % Permanent compression deformation 200%Strain DIN 53504 8 % tensile strength 100%Strain,0.635mm ASTM D412 2.34 Mpa tensile strength 100%Strain,0.635mm DIN 53504 1.40 Mpa tensile strength 300%Strain,0.635mm ASTM D412 4.07 Mpa tensile strength 300%Strain,0.635mm DIN 53504 2.40 Mpa tensile strength Break,0.635mm ASTM D412 7.52 Mpa tensile strength Break,0.635mm DIN 53504 10.0 Mpa Tensile strain Break,0.635mm ASTM D412 720 % Tensile strain Break,0.635mm DIN 53504 900 % tear strength 0.635mm ASTM D624 35.9 kN/m tear strength 0.635mm DIN 53515 25 kN/m Permanent compression deformation 23°C,70hr ASTM D395 40 % Permanent compression deformation 70°C,24hr ASTM D395 80 % Permanent compression deformation 23°C,70hr DIN 53517 35 % Permanent compression deformation 70°C,24hr DIN 53517 60 % Shore hardness ASTM D2632 60 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear resistance -- ASTM D395 43 mm³ Wear resistance -- DIN 53516 43 mm³
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature Internal Method 98.9to130 °C TMA High:635.0μm Internal Method 145 °C TMA Low:635.0μm Internal Method 110 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Melt Volume Flow Rate (MVR) 160°C/8.7kg 35.0 cm3/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreD,Injection ASTM D2240 15 Shore hardness ShoreA,Injection DIN 53505 55 Shore hardness ShoreD,Injection DIN 53505 15 Shore hardness ShoreA,Injection ASTM D2240 56
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.