برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity ASTM D1003 0.30 % transmissivity Regular ASTM D1003 89.0 % transmissivity Total ASTM D1003 91.0 %
impact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,EnergyatPeakLoad ASTM D3763 42.0 J Dart impact -40°C,EnergyatPeakLoad ASTM D3763 48.0 J Impact strength of cantilever beam gap 23°C ASTM D4218 NoBreak Impact strength of cantilever beam gap -40°C ASTM D4218 NoBreak Impact strength of cantilever beam gap 23°C ASTM D256 80 J/m Impact strength of cantilever beam gap -40°C ASTM D256 40 J/m
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength Yield,23°C ASTM D790 69.0 Mpa Bending modulus 23°C ASTM D790 2000 Mpa elongation Break,23°C ASTM D638 320 % elongation Yield,23°C ASTM D638 5.0 % tensile strength Break,23°C ASTM D638 51.0 Mpa tensile strength Yield,23°C ASTM D638 47.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 65.0 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 73.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm ASTM D955 0.20-0.60 % density ASTM D792 1.20 g/cm³
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ASTM D785 103