physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	flow, 24 h	ISO 294	0.17 %
	Shrinkage rate	flow, 24 h	ASTM D 955	0.2 %
		Shrinkage rate	xflow, 24，Across Flow	ASTM D 955	0.8 %
		Shrinkage rate	Shrinkage rate	xflow, 24，Across Flow	ISO 294	0.82 %
Water absorption rate	50% RH,	ASTM D 570	0.33 %

other	شرایط آزمون	روش آزمون	نتیجه آزمون
purpose			IT办公

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	/，断裂	ASTM D638	196 Mpa
tensile strength	tensile strength	/，断裂	ISO 527	196 Mpa
elongation at break	/	ASTM D638	2.5 %
elongation at break	elongation at break	/	ISO 527	2.5 %
bending strength	/	ASTM D790	280 Mpa
bending strength	bending strength	/	ISO 178	280 Mpa
Flexural modulus	/	ASTM D790	10820 Mpa
Flexural modulus	Flexural modulus	/	ISO 178	11230 Mpa
coefficient of friction	Dynamic	ASTM D 3702	0.46 /
coefficient of friction	coefficient of friction	Static C	ASTM D 3702	0.49 /
Wear factor	Wear Fa	ASTM D 3702	6 E-10 in5·min/ft·lb·hr

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23℃ (73℉)	ISO 180/1A	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃ (73℉)80104	ASTM D256	117 J/m
Suspended wall beam without notch impact strength	23℃ (73℉)80104	ISO 180/1U	70 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23℃ (73℉)	ASTM D4812	1014 J/m
Instrumented dart impact energy peak at 23 ℃ (73 ℉)	/	ASTM D3763	7 J
Multi axis impact	/	ISO 6603	3 J