Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
60 kJ/m²
Charpy Notched Impact Strength
-40°C
ISO 179/1eA
5.0 kJ/m²
Charpy Notched Impact Strength
23°C
ISO 179/1eA
6.0 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.8mm
UL 94
HB
UL flame retardant rating
1.5mm
UL 94
HB
UL flame retardant rating
0.8mm
IEC 60695-11-10,-20
HB
UL flame retardant rating
1.5mm
IEC 60695-11-10,-20
HB
FMVSS flammability
FMVSS302
B
Burning rate
1.00mm
ISO 3795
<100 mm/min
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
5500 Mpa
tensile strength
Break
ISO 527-2
125 Mpa
Tensile strain
Break
ISO 527-2
3.5 %
Bending modulus
ISO 178
4900 Mpa
bending strength
ISO 178
210 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
277 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
230 °C
Melting temperature
ISO 11357-3
300 °C
Linear coefficient of thermal expansion
MD:--
ISO 11359-2
3.4E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:-40to23°C
ISO 11359-2
3.4E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:--
ISO 11359-2
7.3E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:-40to23°C
ISO 11359-2
7E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.25 g/cm³
Shrinkage rate
TD
ISO 294-4
0.70 %
Shrinkage rate
MD
ISO 294-4
0.40 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+15 ohms·cm