برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C3 ISO 180/1U 24 kJ/m² Suspended wall beam without notch impact strength 23°C ASTM D4812 360 J/m Dart impact 23°C,EnergyatPeakLoad ASTM D3763 9.40 J Dart impact -- ISO 6603-2 2.47 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear factor Washer ASTM D3702Modified 60.0 10^-10in^5-min/ft-lb-hr bending strength -- ASTM D790 179 Mpa Bending modulus -- ISO 178 10800 Mpa Bending modulus -- ASTM D790 9930 Mpa elongation Break ISO 527-2 1.5 % Tensile modulus -- ISO 527-2/1 9540 Mpa Tensile modulus --2 ASTM D638 10200 Mpa Friction coefficient Static ASTM D3702Modified 0.36 Friction coefficient Dynamic ASTM D3702Modified 0.46 bending strength -- ISO 178 138 Mpa elongation Break ASTM D638 1.9 % tensile strength Break ISO 527-2 89.0 Mpa tensile strength Break ASTM D638 129 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion TD:-40to40°C ASTME831 3.5E-05 cm/cm/°C Linear coefficient of thermal expansion MD:-40to40°C ASTME831 2.3E-05 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan4 ISO 75-2/Af 210 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 208 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate Equilibrium,23°C,50%RH ISO 62 0.50 % Water absorption rate 24hr,50%RH ASTM D570 0.29 % Shrinkage rate MD:24hr ISO 294-4 0.10-0.30 % Shrinkage rate TD:24hr ISO 294-4 0.30-0.60 % Shrinkage rate TD:24hr ASTM D955 0.30-0.60 % Shrinkage rate MD:24hr ASTM D955 0.10-0.40 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.