برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 15 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 2.0 % tensile strength ASTM D638/ISO 527 72 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 83 Bending modulus ASTM D790/ISO 178 3430 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 105 kg/cm²(MPa)[Lb/in²] tensile strength Yield ISO 527-2/5 69.9 Mpa Bending modulus ISO 178 3700 Mpa bending strength ISO 178 130 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 90 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 110 ℃(℉) Vicat softening temperature ISO 306/B 103 °C RTI Elec UL 746 50.0 °C RTI Imp UL 746 50.0 °C RTI UL 746 50.0 °C Ball Pressure Test EMAC 95 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 87.7 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.08 kg·cm/cm(J/M)ft·lb/in melt mass-flow rate ASTM D1238/ISO 1133 12.5 g/10min melt mass-flow rate 220°C/10.0kg ISO 1133 12 g/10min Melt Volume Flow Rate (MVR) 220°C/10.0kg ISO 1133 13.0 cm3/10min Shrinkage rate MD ASTM D955 0.40-0.60 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.