Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation at break		ISO 527-2	35 %
Shore hardness		ISO 868	A97/D65
Flexural modulus		ISO 178	1750 Mpa
tensile strength	屈服	ISO 527-2	30 Mpa
Impact strength of simply supported beam without notch	＋23℃/－30℃	ISO 178/1eU	80/25 KJ/m
Yang's modulus		ISO 527-2	1700 Mpa
Impact strength of cantilever beam gap	＋23℃	ISO 180/1A	3 KJ/m
elongation	屈服	ISO 527-2	2 %
Impact strength of cantilever beam gap	23℃	ASTM D-256	30 J/m
bending strength		ISO 178	40 Mpa
Charpy Notched Impact Strength	＋23℃/－30℃	ISO 179/1eA	-/3.5 KJ/m

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		IEC 93	>10 Ω.cm
dielectric constant	10Hz-1MHz	IEC 250	2.5
Surface Resistivity		IEC 243/1	>10

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8MPa，HDT	ISO 75	64 °C
Injection mold temperature			30-50 °C
Injection molding melting temperature			180-250 °C
UL	厚度3.2mm/1.6mm	UL 94	HB/HB CLASS