Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
110 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
110 kJ/m²
Suspended wall beam without notch impact strength
-30°C
ISO 180/1U
95 kJ/m²
Suspended wall beam without notch impact strength
23°C
ISO 180/1U
95 kJ/m²
Multi axis Instrumented Impact Energy
-30°C
ISO 6603-2
4.70 J
Multi axis Instrumented Impact Energy
23°C
ISO 6603-2
9.10 J
Multi axis Instrumented Peak Impact Force
-30°C
ISO 6603-2
1100 N
Multi axis Instrumented Peak Impact Force
23°C
ISO 6603-2
1450 N
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Bending strain
23°C
ISO 178/A
5.0 %
Tensile modulus
23°C
ISO 527-2/1
11000 Mpa
tensile strength
Break,23°C
ISO 527-2/5
160 Mpa
Tensile strain
Break,23°C
ISO 527-2/5
5.5 %
Nominal tensile fracture strain
23°C
ISO 527-2/50
-- %
Bending modulus
23°C
ISO 178/A
10100 Mpa
bending strength
3.5%Strain,23°C
ISO 178/A
235 Mpa
bending strength
23°C4
ISO 178/A
255 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
203 °C
Melting temperature
ISO 11357-3
220 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
TD:120°C,4hr,2.00mm3
ISO 2577
0.13 %
Shrinkage rate
MD:280°C,2.00mm2
ISO 2577
0.25 %
Shrinkage rate
MD:120°C,4hr,2.00mm3
ISO 2577
0.030 %
Shrinkage rate
TD:280°C,2.00mm2
ISO 2577
0.73 %
Supplementary Information
شرایط آزمون
روش آزمون
نتیجه آزمون
ISO Shortcut
ISO 1874
PA6-HI.GHR.14-110.GF40