thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	136 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	124 °C
vicat		ASTM D15254	142 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	6.3E-05 cm/cm/°C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服	ASTM D638	60.0 Mpa
tensile strength	tensile strength	断裂	ASTM D638	61.0 Mpa
elongation	屈服	ASTM D638	6.0 %
elongation	elongation	断裂	ASTM D638	120 %
flexural modulus	50.0mm跨距	ASTM D790	2670 Mpa
bending strength	屈服,50.0mm跨距	ASTM D790	98.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	23°C,TotalEnergy	ASTM D3763	69.0 J

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17 g/10min
shrinkage rate	MD：3.20mm	内部方法	0.50-0.70 %
Water absorption rate	饱和,23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.15 %