برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D-790 750 kg/cm impact elasticity Notched1/4" ASTM D-256 18 kgcm/cm Bending modulus ASTM D-790 24000 kg/cm Rockwell hardness R-Scale ASTM D-785 105 tensile strength ASTM D-638 480 kg/cm Elongation at Break ASTM D-638 20 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1/18" UL -94 HB Hot deformation temperature Unannealed18.5kg/cm2,1/2" ASTM D-648 89 °C Burning rate 1/16" UL -94 HB Vicat softening temperature 1.000g ASTM D-1525 97 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.004-0.006 mm/mm melt mass-flow rate 220℃/10kg ASTM D-1238 35 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1/18" IEC 707 FH3-35 mm/min Compared to the anti leakage trace index UL -746A PLC 5 High arc combustion index UL -746A PLC 0 High voltage arc tracing rate UL -746A PLC 0 Hot wire ignition UL -746A PLC 5 Arc resistance ASTM D-495 PLC_6
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.