برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity 50.8μm ASTM D1003 3.2 % transparency 50.8μm ASTM D1746 83.0 gloss 20°,50.8μm ASTM D2457 112
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Friction coefficient Itself - Dynamic ASTM D1894 0.15
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature Internal Method 100 °C Vicat softening temperature ASTM D1525 86.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.0 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength MD:Yield,51μm ASTM D882 8.07 Mpa Secant modulus 2%Secant,TD:51μm ASTM D882 96.9 Mpa Secant modulus 2%Secant,MD:51μm ASTM D882 97.4 Mpa Thin film puncture strength 51μm Internal Method 21.9 J/cm³ Thin film puncture strength 51μm Internal Method 82.3 N Thin film puncture strength 51μm Internal Method 8.09 J film thickness 51 µm Blocking force ASTM D3354-89 70 g Initial sealing temperature 51μm Internal Method 85.0 °C Elmendorf tear strength TD:51μm ASTM D1922 730 g Elmendorf tear strength MD:51μm ASTM D1922 560 g Dart impact 51μm ASTM D1709B >830 g elongation TD:Break,51μm ASTM D882 630 % elongation MD:Break,51μm ASTM D882 590 % tensile strength TD:Break,51μm ASTM D882 42.5 Mpa tensile strength MD:Break,51μm ASTM D882 45.4 Mpa tensile strength TD:Yield,51μm ASTM D882 7.17 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.