Instrumented dart impact energy peak at 23 ℃ (73 ℉)
/
ASTM D3763
7 J
Multi axis impact
/
ISO 6603
3 J
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
tensile strength
/,Break
ASTM D638
196 Mpa
tensile strength
/,Break
ISO 527
196 Mpa
Elongation at Break
/
ASTM D638
2.5 %
Elongation at Break
/
ISO 527
2.5 %
bending strength
/
ASTM D790
280 Mpa
bending strength
/
ISO 178
280 Mpa
Bending modulus
/
ASTM D790
10820 Mpa
Bending modulus
/
ISO 178
11230 Mpa
Friction coefficient
Dynamic
ASTM D 3702
0.46 /
Friction coefficient
Static C
ASTM D 3702
0.49 /
Wear factor
Wear Fa
ASTM D 3702
6 E-10 in5·min/ft·lb·hr
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
flow, 24 h
ISO 294
0.17 %
Shrinkage rate
flow, 24 h
ASTM D 955
0.2 %
Shrinkage rate
xflow, 24,Across Flow
ASTM D 955
0.8 %
Shrinkage rate
xflow, 24,Across Flow
ISO 294
0.82 %
Water absorption rate
50% RH,
ASTM D 570
0.33 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.