برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D1822 420 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ASTM D790 106 Mpa Bending modulus ASTM D790 2690 Mpa elongation Break ASTM D638 50to100 % tensile strength ASTM D638 70.3 Mpa Tensile modulus ASTM D638 2480 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 174 °C Linear coefficient of thermal expansion MD ASTM D696 5.6E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr ASTM D570 0.30 % Shrinkage rate MD ASTM D955 0.70 % melt mass-flow rate 343°C/2.16kg ASTM D1238 7.0 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dissipation factor 1MHz ASTM D150 5E-03 Dissipation factor 1kHz ASTM D150 1.3E-03 Dissipation factor 60Hz ASTM D150 1.1E-03 Dielectric constant 1MHz ASTM D150 3.10 Dielectric constant 1kHz ASTM D150 3.14 Dielectric constant 60Hz ASTM D150 3.15 Dielectric strength ASTM D149 17 KV/mm Volume resistivity ASTM D257 5E+16 ohms·cm