Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NB kJ/m²
tensile strength
Yield,23°C
ISO 527-2
60 Mpa
tensile strength
23°C
ISO 527-2
50 Mpa
Elongation at Break
Yield,23°C
ISO 527-2
7.0 %
Elongation at Break
23°C
ISO 527-2
100 %
Tensile modulus
23°C
ISO 527-2
2450 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
108 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
95 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
7E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
7E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD4.0mm
ISO 294-4
0.50-0.70 %
Shrinkage rate
TD4.0mm
ISO 294-4
0.50-0.70 %
Water absorption rate
(23°C,24hr)
ISO 62
0.22 %
melt mass-flow rate
280℃/2.16Kg
ISO 1133
27.0 cm3/10min
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
>1.0E+15 Ω.cm
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
V-0 0.80mm
UL flame retardant rating
UL -94
V-0 3.00mm
Ignition temperature of heating wire
2.00mm
IEC 60695-2-12
960 °C
Relative temperature of heating wire
2.00mm
IEC 60695-2-13
825 °C
UL flame retardant rating
UL -94
V-2 0.40mm