برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
elastomer شرایط آزمون روش آزمون نتیجه آزمون Permanent compression deformation ASTM D395 61 % tear strength ASTM D624 155 kN/m tensile strength 50%Strain ASTM D412 16.7 Mpa
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Taber abraser 1000Cycles ASTM D1044 12.0 mg Compressive modulus ASTM D695 16.3 Mpa Bending modulus ASTM D790 186 Mpa elongation Break ASTM D638 610 % tensile strength Yield ASTM D638 36.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD ASTM D696 1.4E-04 cm/cm/°C Melting temperature DSC 206 °C Vicat softening temperature ASTM D1525 185 °C Brittle temperature ASTM D746 -65.0 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 107 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate Equilibrium,23°C,65%RH ASTM D570 0.38 % Shrinkage rate MD:2.00mm ASTM D955 1.3 % melt mass-flow rate 230°C/2.16kg ASTM D1238 16 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric strength ASTM D149 30 KV/mm Volume resistivity ASTM D257 2E+13 ohms·cm
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreD ASTM D2240 55
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.