برگه داده فنی
مقایسه
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.14 g/cm³ |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.4 % |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 8.5 % |
| Water absorption rate | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.6 % |
| viscosity number | 96% H2SO4 | ISO 307 | 150 cm³/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 79 |
| Rockwell hardness | R 计秤 | ISO 2039-2 | 121 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Limiting Oxygen Index | | ISO 4589-2 | 28 % |
| FMVSS combustion rate | | FMVSS 302 | DNI |
| atomization | F-value (refraction) | ISO 6452 | 99 % |
| atomization | G-value (condensate) | ISO 6452 | 1.0E-4 g |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 3100 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 82.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| Nominal tensile fracture strain | | ISO 527-2 | 25 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- Mpa |
| Flexural modulus | | ISO 178 | 2800 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.5 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt density | | | 0.970 g/cm³ |
| Ejection Temperature | | | 190 °C |
| Specific Heat Capacity of Melt | | | 2790 J/kg/°C |
| Thermal Conductivity of Melt | | | 0.16 W/m/K |
| Emission of Organic Compounds | | VDA 277 | 5.00 µgC/g |
| Odor | | VDA 270 | 3.00 |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 屈服， MD | ISO 527-3 | 4.5 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- ohms |
| Volume resistivity | | IEC 62631-3-1 | 1.0E+12 ohms·m |
| dielectric strength | | IEC 60243-1 | 32 KV/mm |
| relative permittivity | 1 MHz | IEC 62631-2-1 | 3.50 |
| relative permittivity | 100 Hz | IEC 62631-2-1 | 3.80 |
| Dissipation Factor | 100 Hz | IEC 62631-2-1 | 8.0E-3 |
| Dissipation Factor | 1 MHz | IEC 62631-2-1 | 0.018 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 280 to 300 °C |
| Melt Temperature, Optimum | | | 290 °C |
| Temperature | | | 50 to 90 °C |
| Mold Temperature, Optimum | | | 70 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | Drying Recommended | | yes |
| Hold Pressure Time | | | 4.00 s/mm |
| Maximum Screw Tangential Speed | | | 24 m/min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 190 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 70.0 °C |
| Glass Transition Temperature | | ISO 11357-2 | 60.0 °C |
| vicat | | ISO 306/B50 | 240 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| Effective thermal diffusivity coefficient | | | 5.00E-8 m²/s |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.