Impact strength of simply supported beam without notch
ISO 179
58 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.75mm
UL 94
V-0
Burning wire flammability index
3.0mm
IEC 60695-2-12
960 °C
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
23°C
ISO 527-2
9800 Mpa
tensile strength
ASTM D638
150 Mpa
tensile strength
Break,23°C
ISO 527-2
136 Mpa
elongation
Break
ASTM D638
2.3 %
Tensile strain
Break,23°C
ISO 527-2
3.0 %
Bending modulus
ASTM D790
9300 Mpa
Bending modulus
23°C
ISO 178
9600 Mpa
bending strength
ASTM D790
220 Mpa
bending strength
23°C
ISO 178
209 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
258 °C
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
248 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
241 °C
Linear coefficient of thermal expansion
MD
ASTM D696
3E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
TD
Internal Method
1.2 %
Shrinkage rate
MD
Internal Method
0.40 %
Shrinkage rate
吸水率(Saturation,23°C)
Internal Method
-- %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
-- %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Compared to the anti leakage trace index
3.00mm
IEC 60112
PLC 0
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.