Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
43 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
45 kJ/m²
Charpy Notched Impact Strength
-30°C
ISO 179/1eA
7.0 kJ/m²
Charpy Notched Impact Strength
23°C
ISO 179/1eA
8.0 kJ/m²
Bending modulus
23°C
ISO 178
5500 Mpa
bending strength
23°C
ISO 178
200 Mpa
Tensile modulus
23°C
ISO 527-2
6000 Mpa
Elongation at Break
23°C
ISO 527-2
3.00 %
tensile strength
23°C
ISO 527-2
130 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
TD
ISO 11359-2
7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion
MD
ISO 11359-2
3.0E-5 cm/cm/°C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
240 °C
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
250 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.23 g/cm³
melt mass-flow rate
275℃/5.0Kg
ISO 1133
60 cm3/10min
Water absorption rate
(23°C,50RH)
ISO 62
2.20 %
Water absorption rate
(23°C,24hr)
ISO 62
7.00 %
Shrinkage rate
MD2.0mm
ISO 294-4
0.75 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dissipation factor
相对漏电起痕指数
IEC 60112
450 V
Dissipation factor
23°C
IEC 60250
0.014 1MHz
Dielectric constant
23°C
IEC 60250
3.50 1MHz
Dielectric strength
IEC 60243-1
12 KV/mm
Volume resistivity
IEC 60093
1E+10 Ω.cm
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 3.00mm
UL flame retardant rating
UL -94
HB 1.50mm
UL flame retardant rating
UL -94
HB 0.75mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.