Impact strength of simply supported beam without notch
23 ℃
ISO 179/1eU
80 kJ/m²
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
60 kJ/m²
Charpy Notched Impact Strength
23 ℃
ISO 179/1eA
13 kJ/m²
Charpy Notched Impact Strength
-30℃
ISO 179/1eA
11 kJ/m²
Charpy Notched Impact Strength
-40 ℃
ISO 179/1eA
12 kJ/m²
Bending modulus
ISO 178
8200 Mpa
Tensile modulus
ISO 527
9500 Mpa
Fracture strain
ISO 527
3 %
Fracture stress
ISO 527
168 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
Parallel
ISO 11359-1/-2
0.26 E-4/C
Linear coefficient of thermal expansion
Normal
ISO 11359-1/-2
0.83 E-4/C
Melting temperature
10°C/min
ISO 11357-1/-3
218 °C
Hot deformation temperature
1.80MPa
ASTM D790/ISO 178
200 °C
Hot deformation temperature
0.45MPa
ASTM D790/ISO 178
216 °C
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+13 E-4/C
Compared to the anti leakage trace index
3.0mm
UL 746A
PLC 1
UL flame retardant rating
0.75mm
UL 94
HB