برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون gloss 20°,50.8μm ASTM D2457 141 transparency 50.8μm ASTM D1746 83.0 turbidity 50.8μm ASTM D1003 1.1 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 86.0 °C Melting temperature Internal Method 99.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.0 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength MD:Break,51μm ASTM D882 58.6 Mpa tensile strength TD:Break,51μm ASTM D882 44.7 Mpa elongation MD:Break,51μm ASTM D882 620 % elongation TD:Break,51μm ASTM D882 630 % Dart impact 51μm ASTM D1709B >830 g Elmendorf tear strength MD:51μm ASTM D1922 550 g Elmendorf tear strength TD:51μm ASTM D1922 720 g Initial sealing temperature 51μm Internal Method 85.0 °C film thickness 51 µm Thin film puncture strength 51μm Internal Method 8.81 J Thin film puncture strength 51μm Internal Method 92.5 N Thin film puncture strength 51μm Internal Method 22.3 J/cm³ Secant modulus 2%Secant,MD:51μm ASTM D882 91.7 Mpa Secant modulus 2%Secant,TD:51μm ASTM D882 92.4 Mpa tensile strength MD:Yield,51μm ASTM D882 7.24 Mpa tensile strength TD:Yield,51μm ASTM D882 6.89 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.