برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C,3.20mm,Injection ASTM D256 无断裂 Dart impact 23°C,3.20mm,Injection,总能量 ASTM D3763 87.0 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 3.20mm,Injection ASTM D638 2410 Mpa tensile strength Yield,3.20mm,Injection ASTM D638 60.0 Mpa tensile strength Break,3.20mm,Injection ASTM D638 71.0 Mpa elongation Yield,3.20mm,Injection ASTM D638 6.0 % elongation Break,3.20mm,Injection ASTM D638 150 % Bending modulus 3.20mm,Injection ASTM D790 2410 Mpa bending strength 3.20mm,Injection ASTM D790 96.5 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Annealed ASTM D648 143 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 127 °C Hot deformation temperature 1.8MPa,Annealed ASTM D648 140 °C Vicat softening temperature ASTM D15253 148 °C Ball pressure temperature IEC 60335-1 >125 °C Linear coefficient of thermal expansion MD:-40to82°C ASTM D696 6.8E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D955 0.50-0.70 % melt mass-flow rate 300°C/1.2kg ASTM D1238 15 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale,3.20mm,Injection ASTM D785 118