برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break ASTM D638 120 % tensile strength - ASTM D638 9100 Ibf/in Impact strength of cantilever beam gap - ASTM D256 75 Kgf.cm/cm Impact strength of cantilever beam gap - ASTM D256 740 J/m Bending modulus - ASTM D790 313000 Ibf/in Bending modulus - ASTM D790 22000 Kgf/cm Bending modulus - ASTM D790 2160 Mpa bending strength - ASTM D790 12400 Ibf/in bending strength - ASTM D790 870 Kgf/cm bending strength - ASTM D790 85 Mpa tensile strength - ASTM D638 640 Kgf/cm tensile strength - ASTM D638 63 Mpa Impact strength of cantilever beam gap - ASTM D256 14 ft.ibf/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Heat resistance ASTM D257 V-2 Hot deformation temperature 18.6kg/cm ASTM D648 271 ℉ Hot deformation temperature 18.6kg/cm ASTM D648 133 °C melt mass-flow rate 300℃,1.2kg ASTM D1238 20 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257 10 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.