برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C ISO 180/1A 29 kJ/m² Suspended wall beam without notch impact strength 23°C ISO 180/1U 140 kJ/m² Dart impact 23°C,EnergyatPeakLoad ASTM D3763 30.6 J Multi axis Instrumented Impact Energy ISO 6603-2 34.1 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile strain Yield ISO 527-2 5.5 % elongation Break ASTM D638 38 % Bending modulus ASTM D790 2190 Mpa Bending modulus ISO 178 2400 Mpa bending strength ASTM D790 80.3 Mpa bending strength ISO 178 84.1 Mpa Friction coefficient Dynamic ASTM D3702Modified 0.18 Friction coefficient Static ASTM D3702Modified 0.070 Wear factor Washer ASTM D3702Modified 60.0 10^-10in^5-min/ft-lb-hr Tensile modulus ASTM D638 2070 Mpa Tensile modulus ISO 527-2/1 2200 Mpa tensile strength Yield ASTM D638 51.7 Mpa tensile strength Yield ISO 527-2 53.0 Mpa tensile strength Break ASTM D638 47.6 Mpa tensile strength Break ISO 527-2 50.0 Mpa elongation Yield ASTM D638 6.1 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 128 °C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan ISO 75-2/Af 131 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:24hr ASTM D955 0.80-0.90 % Shrinkage rate TD:24hr ISO 294-4 0.88 % Shrinkage rate MD:24hr ISO 294-4 0.83 % Water absorption rate 24hr,50%RH ASTM D570 0.12 % Water absorption rate Equilibrium,23°C,50%RH ISO 62 0.15 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.