Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
160 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
220 kJ/m²
Charpy Notched Impact Strength
-30°C
ISO 179/1eA
12 kJ/m²
Charpy Notched Impact Strength
23°C
ISO 179/1eA
60 kJ/m²
Bending modulus
23°C
ISO 178
2300 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
MD
ISO 11359-2
8E-05 cm/cm/°C
Vicat softening temperature
5.10kg
ISO 306/A50
105 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
99 °C
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
106 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
melt mass-flow rate
线性收缩率
ISO 294-4
0.5-0.7 %
melt mass-flow rate
220℃/10.0Kg
ISO 1133
9 g/10min
density
ISO 1183
1.07 g/cm³
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric constant
IEC 60250
3.1 100HZ
Dissipation factor
IEC 60250
0.05
Dielectric constant
IEC 60250
3 1MHz
Dielectric strength
1.00mm
IEC 60243-1
38 KV/mm
Surface resistivity
IEC 60093
1E+16 Ω.cm
Volume resistivity
IEC 60093
1E+14 Ω.cm
Dissipation factor
IEC 60250
0.09
Dissipation factor
相对漏电起痕指数
IEC 60112
600 V
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Ball Pressure Test
ISO 2039-1
105 Mpa
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Ignition temperature of heating wire
2.00mm
IEC 60695-2-12
700 °C