برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C,3.20mm,Injection ASTM D256 无断裂 Dart impact 23°C,3.20mm,Injection,总能量 ASTM D3763 87.0 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6mm UL 94 HB UL flame retardant rating 3.2mm UL 94 HB Extreme Oxygen Index ASTM D2863 26 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 3.20mm,Injection ASTM D638 2340 Mpa tensile strength Yield,3.20mm,Injection ASTM D638 60.0 Mpa tensile strength Break,3.20mm,Injection ASTM D638 71.0 Mpa elongation Break,3.20mm,Injection ASTM D638 150 % Bending modulus 3.20mm,Injection ASTM D790 2410 Mpa bending strength 3.20mm,Injection ASTM D790 96.5 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Annealed,3.99mm ASTM D648 143 °C Hot deformation temperature 1.8MPa,Unannealed,3.99mm ASTM D648 127 °C Hot deformation temperature 1.8MPa,Annealed,3.99mm ASTM D648 140 °C Vicat softening temperature ASTM D15254 148 °C Linear coefficient of thermal expansion MD:-40to80°C ASTM D696 6.8E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2kg ASTM D1238 15 g/10min Shrinkage rate MD ASTM D955 0.50-0.70 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant 60Hz ASTM D150 3.00 Dielectric constant 1MHz ASTM D150 3.00 Dissipation factor 60Hz ASTM D150 1E-03 Dissipation factor 1MHz ASTM D150 2E-03 Volume resistivity ASTM D257 2E+17 ohms·cm Dielectric strength ASTM D149 17 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale,3.20mm,Injection ASTM D785 118