PBT VALOX™ 310SEO BK1066 SABIC INNOVATIVE US
56
- Properties:Flame retardant
- Usages:Electrical fieldElectronic fieldIndustrial applicationsswitchShell
- Certificates:UL
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Specific Volume | ASTM D792 | 0.710 | cm³/g | |
Melt Mass-Flow Rate | 250°C/2.16 kg | ASTM D1238 | 8.6 | g/10 min |
Melt Volume flow Rate | 250°C/2.16 kg | ISO 1133 | 8.00 | cm3/10min |
Modeling Shrinkage | 流动 2 | 内部方法 | 1.1 到 1.8 | % |
流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 到 1.6 | % | |
流动 : 3.20 mm | 内部方法 | 1.5 到 2.3 | % | |
流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 到 2.3 | % | |
横向流动 2 | 内部方法 | 0.90 到 1.9 | % | |
横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 到 1.7 | % | |
横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 到 2.4 | % | |
Moisture Absorption | 饱和, 23°C | ISO 62 | 0.36 | % |
平衡, 23°C, 50% RH | ISO 62 | 0.080 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Modulus | -- 3 | ASTM D638 | 2820 | Mpa |
-- | ISO 527-2/1 | 2800 | Mpa | |
Tensile Strength | 屈服 4 | ASTM D638 | 58.0 | Mpa |
屈服 | ISO 527-2/50 | 58.0 | Mpa | |
断裂 4 | ASTM D638 | 52.0 | Mpa | |
断裂 | ISO 527-2/50 | 40.0 | Mpa | |
Tensile Elongation | 屈服 4 | ASTM D638 | 5.0 | % |
屈服 | ISO 527-2/50 | 5.0 | % | |
断裂 4 | ASTM D638 | 18 | % | |
断裂 | ISO 527-2/50 | 18 | % | |
Flexural Modulus | 50.0 mm 跨距 5 | ASTM D790 | 2620 | Mpa |
-- 6 | ISO 178 | 2600 | Mpa | |
Flexural Stress | -- 6, 7 | ISO 178 | 90.0 | Mpa |
屈服, 50.0 mm 跨距 5 | ASTM D790 | 101 | Mpa | |
Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 | mg |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Deflection Temperature Under Load | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 | °C |
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Be | 150 | °C | |
1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 74.0 | °C | |
1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 71.0 | °C | |
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Ae | 60.0 | °C | |
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 73.0 | °C | |
Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B50, ISO 306/B120 | 170 | °C |
-- | ISO 306/A50 | 212 | °C | |
Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 | |
Coefficient of Linear Thermal Expansion | 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C |
流动 : 60 到 138°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C | |
流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
横向 : -40 到 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C | |
横向 : -40°C | ISO 11359-2 | 7.3E-5 | cm/cm/°C | |
横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
Thermal Conductivity | ISO 8302 | 0.24 | W/m/K | |
RTI Elec | UL 746 | 120 | °C | |
RTI Imp | UL 746 | 120 | °C | |
RTI | UL 746 | 140 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
Volume Resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 24 | KV/mm |
3.20 mm, in Air | ASTM D149 | 18 | KV/mm | |
0.800 mm, 在油中 | IEC 60243-1 | 35 | KV/mm | |
1.00 mm 12 | IEC 60243-1 | 18 | KV/mm | |
1.60 mm, 在油中 | IEC 60243-1 | 25 | KV/mm | |
3.20 mm, 在油中 | IEC 60243-1 | 17 | KV/mm | |
Relative Permittivity | 50 Hz | IEC 60250 | 2.90 | |
60 Hz | IEC 60250 | 2.90 | ||
100 Hz | IEC 60250 | 3.10 | ||
1 MHz | IEC 60250 | 2.80 | ||
Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 | |
60 Hz | IEC 60250 | 1.0E-3 | ||
100 Hz | IEC 60250 | 2.0E-3 | ||
1 MHz | IEC 60250 | 0.013 | ||
Arc Resistance | ASTM D495 | PLC 6 | ||
Comparative Tracking Index | UL 746 | PLC 3 | ||
-- | IEC 60112 | 175 | V | |
解决方案 B | IEC 60112 | 100 | V | |
High Amp Arc Ignition | UL 746 | PLC 0 | ||
High Voltage Arc Tracking Rate | UL 746 | PLC 6 | ||
UL 746 | PLC 4 | |||
Hot-wire Ignition | UL 746 | PLC 2 |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Temperature | 120 | °C | ||
Drying Time | 3.0 到 4.0 | hr | ||
Suggested Max Moisture | 0.020 | % | ||
Suggested Shot Size | 40 到 80 | % | ||
Rear Temperature | 230 到 250 | °C | ||
Middle Temperature | 240 到 255 | °C | ||
Front Temperature | 245 到 260 | °C | ||
Nozzle Temperature | 240 到 255 | °C | ||
Processing (Melt) Temp | 245 到 260 | °C | ||
Mold Temperature | 50 到 75 | °C | ||
Back Pressure | 0.300 到 0.700 | Mpa | ||
Screw Speed | 50 到 100 | rpm | ||
Vent Depth | 0.013 到 0.025 | mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
23°C | ISO 179/1eU | 无断裂 | ||
Unnotched Izod Impact Strength | 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
-30°C 9 | ISO 180/1U | 无断裂 | ||
Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 200 | J |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | R 计秤 | ISO 2039-2 | 120 | |
Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 105 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 0.71 mm | UL 94 | V-0 | |
3.0 mm | UL 94 | 5VA | ||
Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 | °C |
Oxygen Index | ISO 4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.