PC 124R-111 SABIC INNOVATIVE SPAIN

LEXAN™

Non specific food

transparent,High mobility

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness		R-Scale	ASTM D785	118

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C
Hot deformation temperature		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	129 °C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5 cm/cm/°C
RTI		UL 746	130 °C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
specific heat		ASTM C351	1250 J/kg/°C
thermal conductivity		ASTM C177	0.19 W/m/K
Vicat softening temperature		ASTM D15255	154 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Bending modulus	50.0 mm Span	ASTM D790	2340 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	96.0 Mpa
elongation	Yield	ASTM D638	7.0 %
elongation		Break	ASTM D638	130 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0 mg
tensile strength	Yield	ASTM D638	62.0 Mpa
tensile strength		Break	ASTM D638	68.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Compared to the anti leakage trace index		UL 746	PLC 2
Dielectric constant	1 MHz	ASTM D150	2.96
		50 kHz	ASTM D150	3.17
		60 Hz	ASTM D150	3.17
Dielectric strength	3.20 mm, in Air	ASTM D149	15 KV/mm
Dissipation factor	1 MHz	ASTM D150	0.010
		60 Hz	ASTM D150	9.0E-4
		50 Hz	ASTM D150	9.0E-4
High arc combustion index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	> 1.0E+17 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	18 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Specific volume		ASTM D792	0.830 cm³/g
Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35 %
		24 hr	ASTM D570	0.15 %
		Equilibrium, 100°C	ASTM D570	0.58 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Dart impact	23°C	ASTM D3029	169 J
Impact strength of cantilever beam gap		ASTM D1822	546 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
UL flame retardant rating	1.5 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.025 to 0.076 mm
Mold temperature			70 to 95 °C
Processing (melt) temperature			280 to 305 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			275 to 300 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			280 to 305 °C
Temperature at the rear of the barrel			260 to 280 °C
Temperature in the middle of the barrel			270 to 295 °C

optical performance	Test Condition	Test Method	SABIC INNOVATIVE SPAIN/124R-111
Refractive index		ASTM D542	1.586
transmissivity	2540 μm	ASTM D1003	88.0 %
turbidity	2540 μm	ASTM D1003	1.0 %