PPO SE1GFN2-701 SABIC INNOVATIVE US

NORYL™

Electronic communication accessories,Electronic communication accessories

enhance,Glass fiber reinforced

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	142 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	134 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	133 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	3.0E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	2.5E-5 cm/cm/°C
Vicat softening temperature	--	ASTM D15259	142 °C
Vicat softening temperature		--	ISO 306/B120	144 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
Bending modulus	50.0 mm Span5	ASTM D790	5500 Mpa
Bending modulus		--6	ISO 178	5600 Mpa
bending strength	--6,7	ISO 178	150 Mpa
bending strength		Yield, 50.0 mm Span5	ASTM D790	140 Mpa
elongation	Break4	ASTM D638	3.0 %
elongation		Break	ISO 527-2/50	2.5 %
Tensile modulus	--3	ASTM D638	7100 Mpa
Tensile modulus		--	ISO 527-2/1	6400 Mpa
tensile strength	Break	ISO 527-2/50	100 Mpa
tensile strength		Break4	ASTM D638	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
Dielectric constant	1 MHz	IEC 60250	2.90
Dielectric constant		1 MHz	ASTM D150	2.93
Dielectric strength	1.60 mm, in Oil	ASTM D149	26 KV/mm
Dielectric strength		1.50 mm, in Oil	IEC 60243-1	26 KV/mm
Dissipation factor	1 MHz	ASTM D150	3.4E-3
Surface resistivity		ASTM D257	1.3E+17 ohms
Volume resistivity		ASTM D257	2.0E+16 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.5 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	3.00 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.20 - 0.50 %
Water absorption rate	24 hr, 23°C2	ISO 62	0.040 %
Water absorption rate		24 hr, 23°C	ISO 62	0.11 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
Dart impact	23°C, Total Energy	ASTM D3763	18.0 J
Suspended wall beam without notch impact strength	-30°C8	ISO 180/1U	27 kJ/m²
		23°C	ASTM D4812	520 J/m
		23°C8	ISO 180/1U	28 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
UL flame retardant rating	1.5 mm	UL 94	V-1

injection	Test Condition	Test Method	SABIC INNOVATIVE US/SE1GFN2-701
Back pressure			0.300 to 0.700 Mpa
drying temperature			110 to 120 °C
drying time			3.0 to 4.0 hr
Mold temperature			80 to 110 °C
Processing (melt) temperature			300 to 325 °C
Screw speed			20 to 100 rpm
Spray nozzle temperature			300 to 325 °C
Suggested injection volume			30 to 70 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			290 to 325 °C
Temperature at the rear of the barrel			265 to 315 °C
Temperature in the middle of the barrel			275 to 320 °C