PA66 R530H ASCEND USA

Vydyne®

Automotive sector,Engine hood parts

Glass fiber reinforced,Chemical resistance,Hydrolysis resistance,Fatigue resistance,Thermal stability,Lubricity,Antifreeze,Solvent resistance,High mobility,Oil resistant

Plastic Datasheets

thermal performance	Test Condition	Test Method	ASCEND USA/R530H
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	250 °C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.2E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
Melting temperature		ISO 11357-3	260 °C
RTI Elec	3.0mm	UL 746	140 °C
		0.75mm	UL 746	140 °C
		1.5mm	UL 746	140 °C
RTI Imp	1.5mm	UL 746	120 °C
		3.0mm	UL 746	120 °C
		0.75mm	UL 746	120 °C
RTI Str	3.0mm	UL 746	140 °C
		1.5mm	UL 746	140 °C
		0.75mm	UL 746	125 °C

mechanical properties	Test Condition	Test Method	ASCEND USA/R530H
Bending modulus	23°C	ISO 178	9600 Mpa
bending strength	23°C	ISO 178	270 Mpa
Poisson's Ratio	23°C	ISO 527	0.40
Tensile modulus	23°C	ISO 527-2	10000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ISO 527-2	195 Mpa

Electrical performance	Test Condition	Test Method	ASCEND USA/R530H
Arc resistance	3.00mm	ASTM D495	PLC6
Compared to the anti leakage trace index	3.00mm	IEC 60112	V
Dielectric strength	1.00mm	IEC 60243	20 KV/mm
High arc combustion index	1.5mm	UL 746	PLC 0
		0.75mm	UL 746	PLC 0
		3.0mm	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Hot wire ignition	0.75mm	UL 746	PLC 4
		3.0mm	UL 746	PLC 4
		1.5mm	UL 746	PLC 3
Volume resistivity	3.00mm	IEC 60093	1E+13 ohms·cm

Physical properties	Test Condition	Test Method	ASCEND USA/R530H
density		ISO 1183	1.37 g/cm³
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90 %
Shrinkage rate		MD:23°C,2.00mm	ISO 294-4	0.40 %
Water absorption rate	Equilibrium,50%RH	ISO 62	1.9 %
Water absorption rate		23°C,24hr	ISO 62	0.90 %

impact performance	Test Condition	Test Method	ASCEND USA/R530H
Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²
Charpy Notched Impact Strength		23°C	ISO 179	11 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
Impact strength of cantilever beam gap		-30°C	ISO 180	10 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	65 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	75 kJ/m²

flammability	Test Condition	Test Method	ASCEND USA/R530H
Burning wire flammability index	3.0mm	IEC 60695-2-12	675 °C
		1.5mm	IEC 60695-2-12	675 °C
		0.75mm	IEC 60695-2-12	675 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	700 °C
		1.5mm	IEC 60695-2-13	700 °C
		0.75mm	IEC 60695-2-13	700 °C
UL flame retardant rating	0.75mm	UL 94	HB
		3.0mm	UL 94	HB
		1.5mm	UL 94	HB