Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PBT GP-2306FY LG GUANGZHOU

LUPOX®

Electronic field,Electrical field,Electrical/Electronic Applications

Glass fiber reinforced,Flame retardant,Filler: Glass fiber reinf,30% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	LG GUANGZHOU/GP-2306FY
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	205 °C
Melting temperature		ASTM D3418	223 °C
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	140 °C
RTI Str		UL 746	140 °C

mechanical properties	Test Condition	Test Method	LG GUANGZHOU/GP-2306FY
Bending modulus	3.20mm	ASTM D790	9810 Mpa
bending strength	Yield,3.20mm	ASTM D790	162 Mpa
elongation	Break,3.20mm	ASTM D638	2.0 %
tensile strength	Yield,3.20mm	ASTM D638	108 Mpa

Electrical performance	Test Condition	Test Method	LG GUANGZHOU/GP-2306FY
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI)4	UL 746	PLC 2
Dielectric strength	23°C,1.00mm	ASTM D149	28 KV/mm
Volume resistivity	23°C	ASTM D257	1E+17 ohms·cm

Physical properties	Test Condition	Test Method	LG GUANGZHOU/GP-2306FY
melt mass-flow rate	265°C/5.0kg	ASTM D1238	8.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-1.0 %
Water absorption rate	23°C,24hr	ASTM D570	0.080 %

flammability	Test Condition	Test Method	LG GUANGZHOU/GP-2306FY
UL flame retardant rating	3.0mm	UL 94	V-0
		1.5mm	UL 94	V-0
		0.71mm	UL 94	V-0