PA6/66 BK6235LD Dongguan Shengtai
55
- Unit Price:
- $3150 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan Shengtai New Material Technology Co., Ltd.
+86 159****88
3292********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Overview of materials for Nylon 6, 30% Glass Fiber Filled |
---|
Polymer; Thermoplastic; Nylon (Polyamide PA); Nylon 6 (PA6); Nylon 6, 30% Glass Fiber Filled
|
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
|
Click here to view all available suppliers for this material.
Please click here if you are a supplier and would like information on how to add your listing to this material. |
Add to Folder:
|
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.20 - 1.67 g/cc | 0.0434 - 0.0603 lb/in³ | Average value: 1.37 g/cc Grade Count:1079 |
1.136 - 1.20 g/cc @Temperature 220 - 270 °C |
0.04104 - 0.0434 lb/in³ @Temperature 428 - 518 °F |
Average value: 1.17 g/cc Grade Count:10 | |
Filler Content | 25.0 - 33.0 % | 25.0 - 33.0 % | Average value: 29.8 % Grade Count:162 |
Water Absorption | 0.130 - 9.00 % | 0.130 - 9.00 % | Average value: 2.71 % Grade Count:442 |
Moisture Absorption at Equilibrium | 0.170 - 7.10 % | 0.170 - 7.10 % | Average value: 1.97 % Grade Count:340 |
0.700 - 2.50 % @Temperature 70.0 - 70.0 °C |
0.700 - 2.50 % @Temperature 158 - 158 °F |
Average value: 1.68 % Grade Count:44 | |
0.550 - 1.55 % @Temperature 70.0 - 70.0 °C |
0.550 - 1.55 % @Temperature 158 - 158 °F |
Average value: 1.68 % Grade Count:1 | |
0.550 - 1.55 % @Time 180000 - 1.44e+6 sec |
0.550 - 1.55 % @Time 50.0 - 400 hour |
Average value: 1.68 % Grade Count:1 | |
Water Absorption at Saturation | 1.00 - 8.20 % | 1.00 - 8.20 % | Average value: 6.18 % Grade Count:204 |
Additive Loading | 30.0 - 33.0 % | 30.0 - 33.0 % | Average value: 30.8 % Grade Count:4 |
Viscosity | 2.60 - 50.0 cP | 2.60 - 50.0 cP | Average value: 7.04 cP Grade Count:11 |
30.0 - 500 cP @Temperature 230 - 270 °C |
30.0 - 500 cP @Temperature 446 - 518 °F |
Average value: 196 cP Grade Count:3 | |
30.0 - 500 cP @Shear Rate 100 - 10000 1/s |
30.0 - 500 cP @Shear Rate 100 - 10000 1/s |
Average value: 196 cP Grade Count:3 | |
Viscosity Test | 125 - 150 cm³/g | 1.25 - 1.50 dl/g | Average value: 144 cm³/g Grade Count:14 |
Viscosity Number | 125 - 160 cm³/g | 1.25 - 1.60 dl/g | Average value: 142 cm³/g Grade Count:19 |
Maximum Moisture Content | 0.0200 - 0.200 | 0.0200 - 0.200 | Average value: 0.157 Grade Count:47 |
Linear Mold Shrinkage | 0.000500 - 0.0650 cm/cm | 0.000500 - 0.0650 in/in | Average value: 0.00417 cm/cm Grade Count:780 |
0.00100 - 0.00300 cm/cm @Temperature 80.0 - 80.0 °C |
0.00100 - 0.00300 in/in @Temperature 176 - 176 °F |
Average value: 0.00215 cm/cm Grade Count:13 | |
Linear Mold Shrinkage, Transverse | 0.00100 - 0.0650 cm/cm | 0.00100 - 0.0650 in/in | Average value: 0.00763 cm/cm Grade Count:430 |
0.00500 - 0.00700 cm/cm @Temperature 80.0 - 80.0 °C |
0.00500 - 0.00700 in/in @Temperature 176 - 176 °F |
Average value: 0.00638 cm/cm Grade Count:13 | |
Melt Flow | 1.00 - 101 g/10 min | 1.00 - 101 g/10 min | Average value: 25.5 g/10 min Grade Count:108 |
Spiral Flow | 50.0 - 715 cm | 19.7 - 281 in | Average value: 102 cm Grade Count:20 |
Ash | 25.0 - 36.0 % | 25.0 - 36.0 % | Average value: 30.7 % Grade Count:33 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell L | 102 - 115 | 102 - 115 | Average value: 112 Grade Count:5 |
Hardness, Rockwell M | 80.0 - 121 | 80.0 - 121 | Average value: 101 Grade Count:20 |
Hardness, Rockwell R | 82.0 - 122 | 82.0 - 122 | Average value: 119 Grade Count:147 |
12.0 - 12.0 @Temperature 80.0 - 80.0 °C |
12.0 - 12.0 @Temperature 176 - 176 °F |
Average value: 12.0 Grade Count:2 | |
Hardness, Shore D | 76.0 - 89.0 | 76.0 - 89.0 | Average value: 81.7 Grade Count:10 |
Hardness, Shore M | 100 | 100 | Average value: 100 Grade Count:3 |
Ball Indentation Hardness | 70.0 - 280 MPa | 10200 - 40600 psi | Average value: 171 MPa Grade Count:121 |
Tensile Strength, Ultimate | 14.5 - 230 MPa | 2100 - 33400 psi | Average value: 139 MPa Grade Count:866 |
20.0 - 283 MPa @Temperature -40.0 - 150 °C |
2900 - 41000 psi @Temperature -40.0 - 302 °F |
Average value: 120 MPa Grade Count:29 | |
125 - 150 MPa @Temperature 70.0 - 70.0 °C |
18100 - 21800 psi @Temperature 158 - 158 °F |
Average value: 120 MPa Grade Count:1 | |
125 - 150 MPa @Time 180000 - 1.44e+6 sec |
18100 - 21800 psi @Time 50.0 - 400 hour |
Average value: 120 MPa Grade Count:1 | |
30.0 - 170 MPa @Strain 1.00 - 2.00 % |
4350 - 24700 psi @Strain 1.00 - 2.00 % |
Average value: 120 MPa Grade Count:1 | |
30.0 - 170 MPa @Temperature -20.0 - 150 °C |
4350 - 24700 psi @Temperature -4.00 - 302 °F |
Average value: 120 MPa Grade Count:1 | |
Tensile Strength, Yield | 50.0 - 193 MPa | 7250 - 28000 psi | Average value: 148 MPa Grade Count:234 |
111 - 214 MPa @Temperature -40.0 - 80.0 °C |
16100 - 31000 psi @Temperature -40.0 - 176 °F |
Average value: 176 MPa Grade Count:2 | |
Elongation at Break | 1.00 - 180 % | 1.00 - 180 % | Average value: 4.46 % Grade Count:968 |
2.40 - 12.0 % @Temperature -40.0 - 150 °C |
2.40 - 12.0 % @Temperature -40.0 - 302 °F |
Average value: 5.08 % Grade Count:22 | |
Elongation at Yield | 1.50 - 14.0 % | 1.50 - 14.0 % | Average value: 3.96 % Grade Count:107 |
4.60 - 7.60 % @Temperature 60.0 - 150 °C |
4.60 - 7.60 % @Temperature 140 - 302 °F |
Average value: 5.99 % Grade Count:2 | |
Modulus of Elasticity | 1.60 - 20.2 GPa | 232 - 2930 ksi | Average value: 8.00 GPa Grade Count:692 |
2.50 - 11.6 GPa @Temperature -40.0 - 150 °C |
363 - 1680 ksi @Temperature -40.0 - 302 °F |
Average value: 5.36 GPa Grade Count:15 | |
Flexural Yield Strength | 40.0 - 8000 MPa | 5800 - 1.16e+6 psi | Average value: 218 MPa Grade Count:760 |
89.0 - 380 MPa @Temperature -40.0 - 121 °C |
12900 - 55100 psi @Temperature -40.0 - 250 °F |
Average value: 196 MPa Grade Count:11 | |
Flexural Modulus | 0.724 - 18.5 GPa | 105 - 2680 ksi | Average value: 7.45 GPa Grade Count:821 |
2.97 - 12.5 GPa @Temperature -40.0 - 121 °C |
431 - 1810 ksi @Temperature -40.0 - 250 °F |
Average value: 5.68 GPa Grade Count:12 | |
Flexural Strain at Break | 2.50 - 8.00 % | 2.50 - 8.00 % | Average value: 4.86 % Grade Count:97 |
Compressive Yield Strength | 120 - 222 MPa | 17400 - 32200 psi | Average value: 162 MPa Grade Count:12 |
70.0 - 250 MPa @Temperature -40.0 - 80.0 °C |
10200 - 36300 psi @Temperature -40.0 - 176 °F |
Average value: 156 MPa Grade Count:2 | |
Poissons Ratio | 0.340 - 0.350 | 0.340 - 0.350 | Average value: 0.346 Grade Count:19 |
Shear Modulus | 3.60 - 4.10 GPa | 522 - 595 ksi | Average value: 3.77 GPa Grade Count:4 |
Shear Strength | 60.0 - 85.0 MPa | 8700 - 12300 psi | Average value: 76.7 MPa Grade Count:3 |
Izod Impact, Notched | 0.370 - 3.36 J/cm | 0.693 - 6.30 ft-lb/in | Average value: 1.24 J/cm Grade Count:322 |
0.700 - 3.84408 J/cm @Temperature -40.0 - 121 °C |
1.31 - 7.20154 ft-lb/in @Temperature -40.0 - 250 °F |
Average value: 1.18 J/cm Grade Count:8 | |
1.01441 - 1.33475 J/cm @Temperature -40.0 - -40.0 °C |
1.90041 - 2.50053 ft-lb/in @Temperature -40.0 - -40.0 °F |
Average value: 1.18 J/cm Grade Count:8 | |
1.01441 - 1.33475 J/cm @Thickness 3.17 - 3.17 mm |
1.90041 - 2.50053 ft-lb/in @Thickness 0.125 - 0.125 in |
Average value: 1.18 J/cm Grade Count:8 | |
Izod Impact, Unnotched | 0.122 - 5340 J/cm | 0.229 - 10000 ft-lb/in | Average value: 10.0 J/cm Grade Count:53 |
Izod Impact, Notched (ISO) | 1.50 - 182 kJ/m² | 0.714 - 86.6 ft-lb/in² | Average value: 15.4 kJ/m² Grade Count:347 |
3.00 - 35.0 kJ/m² @Temperature -40.0 - -30.0 °C |
1.43 - 16.7 ft-lb/in² @Temperature -40.0 - -22.0 °F |
Average value: 10.5 kJ/m² Grade Count:124 | |
Izod Impact, Unnotched (ISO) | 12.0 kJ/m² - NB | 5.71 ft-lb/in² - NB | Average value: 61.7 kJ/m² Grade Count:124 |
25.0 kJ/m² - NB @Temperature -30.0 - -30.0 °C |
11.9 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F |
Average value: 58.2 kJ/m² Grade Count:76 | |
Charpy Impact Unnotched | 1.20 J/cm² - NB | 5.71 ft-lb/in² - NB | Average value: 7.52 J/cm² Grade Count:547 |
0.700 J/cm² - NB @Temperature -40.0 - -20.0 °C |
3.33 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F |
Average value: 6.24 J/cm² Grade Count:355 | |
Charpy Impact, Notched | 0.200 - 1000 J/cm² | 0.952 - 4760 ft-lb/in² | Average value: 1.48 J/cm² Grade Count:648 |
0.150 - 3.50 J/cm² @Temperature -40.0 - -20.0 °C |
0.714 - 16.7 ft-lb/in² @Temperature -40.0 - -4.00 °F |
Average value: 1.02 J/cm² Grade Count:352 | |
Puncture Energy | 2.00 - 14.0 J | 1.48 - 10.3 ft-lb | Average value: 5.42 J Grade Count:32 |
1.70 - 6.00 J @Temperature -30.0 - -30.0 °C |
1.25 - 4.43 ft-lb @Temperature -22.0 - -22.0 °F |
Average value: 3.10 J Grade Count:28 | |
Coefficient of Friction | 0.150 - 0.610 | 0.150 - 0.610 | Average value: 0.290 Grade Count:8 |
Coefficient of Friction, Static | 0.190 - 0.450 | 0.190 - 0.450 | Average value: 0.322 Grade Count:5 |
Tensile Creep Modulus, 1 hour | 2400 - 92000 MPa | 348000 - 1.33e+7 psi | Average value: 10400 MPa Grade Count:18 |
Tensile Creep Modulus, 1000 hours | 2000 - 6500 MPa | 290000 - 943000 psi | Average value: 3900 MPa Grade Count:22 |
Taber Abrasion, mg/1000 Cycles | 0.350 - 25.0 | 0.350 - 25.0 | Average value: 12.4 Grade Count:4 |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 25.0 - 1.00e+18 ohm-cm | 25.0 - 1.00e+18 ohm-cm | Average value: 5.46e+15 ohm-cm Grade Count:425 |
Surface Resistance | 100 - 1.00e+16 ohm | 100 - 1.00e+16 ohm | Average value: 1.70e+14 ohm Grade Count:253 |
Dielectric Constant | 2.50 - 38.0 | 2.50 - 38.0 | Average value: 5.81 Grade Count:218 |
Dielectric Strength | 7.87 - 80.0 kV/mm | 200 - 2030 kV/in | Average value: 29.3 kV/mm Grade Count:294 |
Dissipation Factor | 0.00500 - 0.850 | 0.00500 - 0.850 | Average value: 0.0875 Grade Count:187 |
Dielectric Loss Index | 0.0220 - 0.240 | 0.0220 - 0.240 | Average value: 0.125 Grade Count:10 |
Arc Resistance | 15.0 - 180 sec | 15.0 - 180 sec | Average value: 117 sec Grade Count:22 |
Comparative Tracking Index | 0.000 - 600 V | 0.000 - 600 V | Average value: 519 V Grade Count:317 |
Hot Wire Ignition, HWI | 15.0 - 60.0 sec | 15.0 - 60.0 sec | Average value: 36.0 sec Grade Count:3 |
High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | Average value: 120 arcs Grade Count:3 |
High Voltage Arc-Tracking Rate, HVTR | 25.4 - 150 mm/min | 1.00 - 5.91 in/min | Average value: 63.5 mm/min Grade Count:3 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 2.50 - 82.0 µm/m-°C | 1.39 - 45.6 µin/in-°F | Average value: 26.1 µm/m-°C Grade Count:286 |
6.00 - 14.0 µm/m-°C @Temperature 55.0 - 160 °C |
3.33 - 7.78 µin/in-°F @Temperature 131 - 320 °F |
Average value: 10.0 µm/m-°C Grade Count:4 | |
CTE, linear, Transverse to Flow | 23.0 - 150 µm/m-°C | 12.8 - 83.3 µin/in-°F | Average value: 81.1 µm/m-°C Grade Count:166 |
110 - 130 µm/m-°C @Temperature 55.0 - 160 °C |
61.1 - 72.2 µin/in-°F @Temperature 131 - 320 °F |
Average value: 120 µm/m-°C Grade Count:4 | |
Specific Heat Capacity | 0.350 - 2.43 J/g-°C | 0.0837 - 0.582 BTU/lb-°F | Average value: 1.57 J/g-°C Grade Count:25 |
2.20 - 2.28 J/g-°C @Temperature 270 - 270 °C |
0.526 - 0.545 BTU/lb-°F @Temperature 518 - 518 °F |
Average value: 2.24 J/g-°C Grade Count:2 | |
Thermal Conductivity | 0.200 - 1.64 W/m-K | 1.39 - 11.4 BTU-in/hr-ft²-°F | Average value: 0.360 W/m-K Grade Count:41 |
0.230 - 0.260 W/m-K @Temperature 270 - 270 °C |
1.60 - 1.80 BTU-in/hr-ft²-°F @Temperature 518 - 518 °F |
Average value: 0.245 W/m-K Grade Count:2 | |
Melting Point | 178 - 325 °C | 352 - 617 °F | Average value: 224 °C Grade Count:630 |
Maximum Service Temperature, Air | 65.0 - 288 °C | 149 - 550 °F | Average value: 157 °C Grade Count:115 |
Deflection Temperature at 0.46 MPa (66 psi) | 125 - 305 °C | 257 - 581 °F | Average value: 216 °C Grade Count:442 |
Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 290 °C | 149 - 554 °F | Average value: 204 °C Grade Count:792 |
Deflection Temperature at 8.0 MPa | 60.0 - 213 °C | 140 - 415 °F | Average value: 128 °C Grade Count:56 |
Vicat Softening Point | 145 - 313 °C | 293 - 595 °F | Average value: 209 °C Grade Count:197 |
Heat Distortion Temperature | 215 - 255 °C | 419 - 491 °F | Average value: 230 °C Grade Count:3 |
Minimum Service Temperature, Air | -60.0 - 120 °C | -76.0 - 248 °F | Average value: 65.3 °C Grade Count:15 |
Glass Transition Temp, Tg | 15.0 - 60.0 °C | 59.0 - 140 °F | Average value: 37.5 °C Grade Count:5 |
Decomposition Temperature | 300 - 350 °C | 572 - 662 °F | Average value: 321 °C Grade Count:20 |
UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 117 °C Grade Count:36 |
UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 103 °C Grade Count:36 |
UL RTI, Mechanical without Impact | 65.0 - 150 °C | 149 - 302 °F | Average value: 116 °C Grade Count:35 |
Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:568 |
Flame Spread | 0.000 - 102 mm/min | 0.000 - 4.02 in/min | Average value: 37.6 mm/min Grade Count:16 |
Oxygen Index | 21.0 - 39.8 % | 21.0 - 39.8 % | Average value: 25.4 % Grade Count:58 |
Glow Wire Test | 550 - 960 °C | 1020 - 1760 °F | Average value: 774 °C Grade Count:159 |
Ignition Temperature | 400 - 470 °C | 752 - 878 °F | Average value: 423 °C Grade Count:18 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 223 °C Grade Count:73 |
Nozzle Temperature | 55.0 - 295 °C | 131 - 563 °F | Average value: 257 °C Grade Count:91 |
Melt Temperature | 210 - 350 °C | 410 - 662 °F | Average value: 266 °C Grade Count:504 |
Mold Temperature | 21.1 - 121 °C | 70.0 - 250 °F | Average value: 83.7 °C Grade Count:517 |
Drying Temperature | 26.7 - 180 °C | 80.0 - 356 °F | Average value: 84.2 °C Grade Count:390 |
Moisture Content | 0.00150 - 1.12 % | 0.00150 - 1.12 % | Average value: 0.144 % Grade Count:216 |
Dew Point | -40.0 - -17.8 °C | -40.0 - 0.000 °F | Average value: -21.5 °C Grade Count:12 |
Injection Pressure | 3.45 - 172 MPa | 500 - 25000 psi | Average value: 73.7 MPa Grade Count:79 |
Vent Depth | 0.00127 - 0.00762 cm | 0.000500 - 0.00300 in | Average value: 0.00238 cm Grade Count:4 |