Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 20 | g/10min |
| Modeling Shrinkage | MD | 内部方法 | 0.40to0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2/1 | 2500 | Mpa |
| Tensile Stress | Yield | ISO527-2/50 | 62.0 | Mpa |
| Tensile Strain | Break | ISO527-2/50 | >20 | % |
| Flexural Modulus | | ISO178 | 2600 | Mpa |
| Flexural Stress | | ISO178 | 93.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 91.0 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 99.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180 | 13 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.2mm | UL94 | V-0 | |
| Flame Rating | 1.5mm | UL94 | 5VB | |
| Flame Rating | 2.5mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.