Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | 23°C | ISO1183 | 1.18 | g/cm³ |
Melt Volume flow Rate | 240°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
Modeling Shrinkage | TD:240°C,3.00mm | ISO2577 | 0.50到0.70 | % |
Modeling Shrinkage | MD:240°C,3.00mm | ISO2577 | 0.50到0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 23°C | ISO527-2/1 | 2700 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2/50 | 60.0 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/50 | 50.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2/50 | 4.0 | % |
Tensile Strain | Break,23°C | ISO527-2/50 | >50 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 100 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 90.0 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 108 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 110 | °C |
Coefficient of Linear Thermal Expansion | MD:23to55°C | ISO11359-2 | 7.6E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD:23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
Relative Permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
Relative Permittivity | 23°C,1MHz | IEC60250 | 3.10 | |
Dissipation Factor | 23°C,100Hz | IEC60250 | 5E-03 | |
Dissipation Factor | 23°C,1MHz | IEC60250 | 7E-03 | |
Comparative Tracking Index | SolutionA | IEC60112 | 350 | V |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 260°C | ISO11443-A | 245 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -30°C | ISO180/A | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/A | 35 | kJ/m² |
Unnotched Izod Impact Strength | 23°C | ISO180 | 无断裂 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.5mm | UL94 | V-0 | |
Flame Rating | 2.0mm | UL94 | 5VB | |
Flame Rating | 3.0mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.