PC/ABS CYCOLOY™ C1200HF-701 SABIC INNOVATIVE NANSHA

Unit Price:
$2682 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
290.6MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	260°C/5.0 kg	ASTM D1238	19	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ASTM D638	2270	Mpa
Tensile Strength	Yield	ASTM D638	57.0	Mpa
Tensile Elongation	Yield	ASTM D638	5.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	100	%
Flexural Modulus	50.0 mm Span	ASTM D790	2340	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	88.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	129	°C
Deflection Temperature Under Load	Deflection Temperature Under Load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	112	°C
Vicat Softening Temperature		ISO 306/B50	130	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 40°C	ASTM E831	7.2E-5	cm/cm/°C
RTI Elec		UL 746	105	°C
RTI Imp		UL 746	80.0	°C
RTI		UL 746	105	°C

Electrical Properties	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 2
High Amp Arc Ignition	UL 746	PLC 1
Hot-wire Ignition	UL 746	PLC 3

Injection	Test Result	Unit
Drying Temperature	100 到 110	°C
Drying Time	3.0 到 4.0	hr
Suggested Max Moisture	0.020	%
Suggested Shot Size	30 到 80	%
Hopper Temperature	60 到 80	°C
Rear Temperature	250 到 290	°C
Middle Temperature	255 到 295	°C
Front Temperature	260 到 300	°C
Nozzle Temperature	275 到 300	°C
Processing (Melt) Temp	275 到 300	°C
Mold Temperature	60 到 90	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.038 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	-30°C, Total Energy	ASTM D3763	54.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	54.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.2 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.