Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
| Modeling Shrinkage | 流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO 527-2/1 | 2400 | Mpa |
| Tensile Stress | Yield | ISO 527-2/50 | 61.0 | Mpa |
| Tensile Stress | Break | ISO 527-2/50 | 56.0 | Mpa |
| Tensile Strain | Yield | ISO 527-2/50 | 6.0 | % |
| Nominal Tensile Strain at Break | | ISO 527-2/50 | > 50 | % |
| Flexural Modulus | | ISO 178 | 2230 | Mpa |
| Flexural Stress | | ISO 178 | 93.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 141 | °C |
| Heat Deflection Temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 129 | °C |
| Vicat Softening Temperature | | ISO 306/B50 | 148 | °C |
| Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | Across Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 | ohms |
| Volume Resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 无断裂 | |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|
| Light Transmittance | 3000 µm | ASTM D1003 | 41.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.