PC PANLITE® AD-5503 TEIJIN JAPAN
38
- Unit Price:
- $5430 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 64.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | /1200 | ||
| Modeling Shrinkage | ASTM D955 | 0.5-0.7 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.2 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 54.0 | cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2/1 | 2450 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | >50 | % | |
| Flexural Modulus | ISO178 | 2400 | Mpa | |
| Flexural Stress | ISO178 | 96.0 | Mpa | |
| Tensile Modulus | ASTM D638/ISO 527 | /2450 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | /63 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | /6 | % | |
| Flexural Modulus | ASTM D790/ISO 178 | /2400 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | /96 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation (Yield) | 50mm/min | ISO 527-1 and ISO 527-2 | 6 | % |
| Izod Impact Strength | 没Notched | ISO 179 | NB | KJ/m |
| Tensile Stress(Yield) | 50mm/min | ISO 527-1 and ISO 527-2 | 63 | Mpa |
| Flexural Modulus | 2mm/min | ISO 178 | 2400 | Mpa |
| Flexural Strength | 2mm/min | ISO 178 | 96 | Mpa |
| Tensile Elongation (Break) | 50mm/min | ISO 527-1 and ISO 527-2 | >50 | % |
| Izod Impact Strength | 带Notched | ISO 179 | 3 | KJ/m |
| Tensile Modulus | 1mm/min | ISO 527-1 and ISO 527-2 | 2450 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load | 1.80MPa | ISO 75-1 and ISO 75-2 | 124 | °C |
| Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 0.7 | X10 |
| Deflection Temperature Under Load | 0.45MPa | ISO 75-1 and ISO 75-2 | 138 | °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 143 | ℃（℉） | |
| Coefficient of Linear Thermal Expansion | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 124 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 143 | °C | |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat Softening Temperature | 50℃/h 50N | ISO 308 | 143 | °C |
| Coefficient of Linear Thermal Expansion | Across Flow | ISO 11359-2 | 0.7 | X10 |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | ||
| ASTM D150/IEC 60250 | 3 | |||
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric Constant | 100Hz | IEO 60250 | 3.1 | |
| 1MHz | IEO 60250 | 3 | ||
| Volume Resistivity | IEO 60250 | >1×10 | Ω.cm | |
| Arc Resistance | 短时间法 | IEO 60243-1 | 30 | MV/m |
| Dissipation Factor (Tangent) | 1MHz | IEO 60250 | 90 | X10 |
| Arc Resistance | IEO 60112 | 250 | ||
| Dissipation Factor (Tangent) | 100Hz | IEO 60250 | 10 | X10 |
| Surface Resistivity | IEO 60250 | >1×10 | Ω | |
| Dielectric Strength | IEC60243-1 | 30 | KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 3.10 | |
| 1MHz | IEC60250 | 3.00 | ||
| Dissipation Factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Comparative Tracking Index | IEC60112 | 250 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | NoBreak |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.585 | ||
| Light Transmittance | 3000µm | ASTMD1003 | 89.0 | % |
| Transmittance | ASTM D1003/ISO 13468 | 89 | % | |
| Index of Refraction | ASTM D542/ISO 489 | 1.585 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ISO 1183 | 1200 | kg/m | |
| Moisture Absorption | 放置在23℃水中24h | ISO 62 | 0.2 | % |
| Melt Volume flow Rate | 300℃负荷1.2kg | ISO1133 | 54 | CM |
| Modeling Shrinkage | Flow | 本公司制订的测定法 | 0.5-0.7 | % |
| Index of Refraction | ASTM D542 | 1.585 | ||
| Transmittance | 试样厚度3mm | ASTM D1003 | 89 | % |
| Modeling Shrinkage | Across Flow | 本公司制订的测定法 | 0.5-0.7 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.