Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | ISO1183 | 1.39 | g/cm³ |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 53 | g/10min |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 46.0 | cm3/10min |
Modeling Shrinkage | MD:3.00mm | | 2.1 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.22 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2 | 2700 | Mpa |
Tensile Stress | Yield | ISO527-2 | 55.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 7.5 | % |
Nominal Tensile Strain at Break | | ISO527-2 | 25 | % |
Flexural Modulus | | ISO178 | 2500 | Mpa |
Flexural Stress | | ISO178 | 81.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO11357-3 | 166 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 156 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
Dielectric Strength | 1.00mm | IEC60243-1 | 36 | KV/mm |
Dielectric Strength | 3.00mm | IEC60243-1 | 19 | KV/mm |
Comparative Tracking Index | | IEC60112 | 600 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179 | 5.0 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 100 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.8mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.