Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.19 | |
Modeling Shrinkage | | ASTM D955 | 0.002-0.006 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 2 | g/10min |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.3 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | | | 93 | % |
Index of Refraction | | | 1.19 | |
Modeling Shrinkage | | | 0.002-0.006 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | | 74.0 | Mpa |
Tensile Elongation | Break | | 5 | % |
Flexural Strength | | | 120.0 | Mpa |
Flexural Modulus | | | 3400 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 73 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 5 | % |
Rockwell Hardness | | ASTM D785 | M100 | |
Flexural Modulus | | ASTM D790/ISO 178 | 3300 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 120 | kg/cm²(MPa)[Lb/in²] |
Impact Strength | 悬臂梁V型Notched | | 0.016 | KJ/m |
Rockwell Hardness | | | 100 | M标度 |
Flexural Modulus | | | 3300 | Mpa |
Flexural Strength | | | 120 | Mpa |
Modeling Shrinkage | | | 0.002-0.006 | cm/cm |
Tensile Elongation | | | 5 | % |
Notched Izod Impact Strength | | | 1.6 | kJ/m² |
Rockwell Hardness | | | 100 | M-scale/R-scale |
Tensile Strength | | | 73 | Mpa |
Tensile Elongation (Break) | | ASTM D638/ISO 527 | 6 | % |
Notched Izod Impact Strength | | ASTM D256/ISO 179 | 1.6 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 经Annealed | | 100 | °C |
Heat Deflection Temperature | | ASTM D648/ISO 75 | 100 | ℃(℉) |
Heat Deflection Temperature | | ASTM D648/ISO 75 | 109 | ℃(℉) |
Coefficient of Linear Thermal Expansion | | | 6×10-5 | cm/cm.℃ |
Heat Deflection Temperature | | | 100 | °C |
Optical | Test Condition | Test Method | Test Result | Unit |
---|
Light Transmittance | | | 93 | % |
Transmittance | | ASTM D1003/ISO 13468 | 92 | % |
Index of Refraction | | ASTM D542/ISO 489 | 1.49 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 条件I | ASTM D1238 | 2 | g/10min |
Melt Mass-Flow Rate | 条件L | | 0.9 | g/10min |
Moisture Absorption | | ASTM D570 | 0.3 | % |
Melt Mass-Flow Rate | | | 2.0 | g/10min |
Moisture Absorption | | | 0.3 | % |
UL | | | 94HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.