Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ASTM D-792 | 无水｜1.59 | |
| Density / Specific Gravity | | ASTM D-792 | 1.3%水｜- | |
| Density / Specific Gravity | 23°C | g/cm³ | 1.59 | -- |
| Modeling Shrinkage | TD:3.00mm3 | % | 0.60到0.90 | -- |
| Modeling Shrinkage | MD:3.00mm4 | % | 0.20到0.50 | -- |
| Moisture Absorption | 23°C,24hr | % | 0.60 | -- |
| Moisture Absorption | Saturation,23°C | % | 4.0 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | -40°C | MPa | 190 | -- |
| Tensile Stress | 23°C | MPa | 165 | |
| Tensile Stress | 80°C | MPa | 110 | -- |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 无水｜1640 | kg/cm2 |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 1.3%水｜1350 | kg/cm2 |
| Tensile Elongation (Break) | 23℃ | ASTM D-638 | 无水｜5 | % |
| Tensile Elongation (Break) | 23℃ | ASTM D-638 | 1.3%水｜5 | % |
| Flexural Stress | 23℃ | ASTM D-790 | 无水｜2490 | kg/cm2 |
| Flexural Stress | 23℃ | ASTM D-790 | 1.3%水｜2000 | kg/cm2 |
| Flexural Modulus | 23℃ | ASTM D-790 | 无水｜93200 | kg/cm2 |
| Flexural Modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 | kg/cm2 |
| Tensile Strain | Break,-40°C | % | 2.5 | -- |
| Tensile Strain | Break,23°C | % | 3.0 | 3.0 |
| Tensile Strain | Break,80°C | % | 4.5 | -- |
| Flexural Modulus | -40°C | MPa | 10200 | -- |
| Flexural Modulus | 23°C | MPa | 9300 | |
| Flexural Modulus | 80°C | MPa | 5500 | -- |
| Flexural Stress | -40°C | MPa | 275 | -- |
| Flexural Stress | 23°C | MPa | 250 | |
| Flexural Stress | 80°C | MPa | 150 | -- |
| Taber Abrasion Resistance | 1000Cycles | mg | 26.0 | -- |
| Izod Impact Strength | 23℃，Unnotched1/8 | | 无水｜65 | kg.cm/cm |
| Izod Impact Strength | 23℃，Unnotched1/8 | | 1.3%水｜70 | kg.cm/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed | °C | 251 | -- |
| Melting Temperature | | °C | 265 | -- |
| Coefficient of Linear Thermal Expansion | MD | cm/cm/°C | 2E-05 | -- |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 无水｜2 | 10-5cm/cm.℃ |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 1.3%水｜- | |
| Deflection Temperature Under Load | 18.6kg/cm2 | ASTM D-648 | 无水｜251 | °C |
| Deflection Temperature Under Load | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | °C |
| Melting Temperature | | 差示扫描测热计DSC法 | 无水｜265 | °C |
| Melting Temperature | | 差示扫描测热计DSC法 | 1.3%水｜- | °C |
| Flame Rating | | UL 94 | 无水｜V-0 | |
| Flame Rating | | UL 94 | 1.3%水｜- | |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | ASTM D-257 | 无水｜8×1014 | Ω.cm |
| Volume Resistivity | | ASTM D-257 | 1.3%水｜8×1013 | Ω.cm |
| Dielectric Strength | 1/8" | ASTM D-149 | 无水｜38 | KV/mm |
| Dielectric Strength | 1/8" | ASTM D-149 | 1.3%水｜33 | KV/mm |
| Comparative Tracking Index | | UL 746 | 无水｜200 | V |
| Comparative Tracking Index | | UL 746 | 1.3%水｜- | V |
| Dissipation Factor | 106Hz | ASTM D-150 | 无水｜0.003-0.009 | |
| Dissipation Factor | 106Hz | ASTM D-150 | 1.3%水｜- | |
| Arc Resistance | 1/8" | ASTM D-495 | 无水｜70-80 | S |
| Arc Resistance | 1/8" | ASTM D-495 | 1.3%水｜- | S |
| Volume Resistivity | | ohms·cm | 1E+15 | 1E+13 |
| Dielectric Strength | | kV/mm | 38 | 33 |
| Dielectric Constant | 23°C,1kHz | | 4.00 | -- |
| Dielectric Constant | 23°C,1MHz | | 0.0100 | -- |
| Arc Resistance | | sec | 70.0 | -- |
| Comparative Tracking Index | CTI | V | 200 | -- |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 | -- |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 9.5 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 65 | |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | | 121 | -- |
| Other Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Reinforcement Content | | | 无水｜30 | wt% |
| Reinforcement Content | | | 1.3%水｜- | wt% |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.40mm | | V-0 | -- |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23℃，24hr | ASTM D-570 | 无水｜0.4 | % |
| Moisture Absorption | 23℃，24hr | ASTM D-570 | 1.3%水｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.