Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ExxonMobil Method | 0.900 | g/cm³ |
Melt Mass-Flow Rate | 230°C/2.16 kg | ASTM D1238 | 4.0 | g/10 min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2/1 | 1200 | Mpa |
Tensile Strength | Yield 3 | ASTM D638 | 23.7 | Mpa |
Tensile Strength | Yield | ISO 527-2/50 | 23.0 | Mpa |
Tensile Elongation | Yield 3 | ASTM D638 | 6.0 | % |
Tensile Elongation | Yield | ISO 527-2/50 | 5.6 | % |
Flexural Modulus | 1% Secant 4 | ASTM D790A | 1210 | Mpa |
Flexural Modulus | 1% Secant 5 | ASTM D790B | 1300 | Mpa |
Flexural Modulus | -- 6 | ISO 178 | 1140 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load | 0.45 MPa, Unannealed | ASTM D648 | 90.6 | °C |
Deflection Temperature Under Load | 0.45 MPa, Unannealed | ISO 75-2/Bf | 82.0 | °C |
Deflection Temperature Under Load | 0.45 MPa, Annealed | ASTM D648 | 112 | °C |
Deflection Temperature Under Load | 1.8 MPa, Unannealed | ISO 75-2/A | 50.2 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.8 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 57 | kJ/m² |
Notched Izod Impact Strength | 23°C | ASTM D256A | 无断裂 | |
Notched Izod Impact Strength | -40°C | ISO 180/1A | 9.0 | kJ/m² |
Notched Izod Impact Strength | -18°C | ISO 180/1A | 11 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO 180/1A | 53 | kJ/m² |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ASTM D785 | 84 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.