PC/PBT XENOY™ 5720U-BK1066 SABIC INNOVATIVE US
13
- Unit Price:
- $6775 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- Huangpu port, China
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan East Asia Plastic Co., Ltd.
+86 138****46
1925********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific Volume | ASTM D792 | 0.850 | cm³/g | |
| Melt Mass-Flow Rate | 250°C/2.16 kg | ASTM D1238 | 3.8 | g/10 min |
| 250°C/5.0 kg | ASTM D1238, ISO 1133 | 11 | g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 | g/10 min | |
| 266°C/5.0 kg | ASTM D1238 | 20 | g/10 min | |
| 250°C/2.16 kg | ISO 1133 | 3.0 | g/10 min | |
| Melt Volume flow Rate | 250°C/2.16 kg | ISO 1133 | 3.00 | cm3/10min |
| 250°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 265°C/2.16 kg | ISO 1133 | 6.00 | cm3/10min | |
| 265°C/5.0 kg | ISO 1133 | 18.0 | cm3/10min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 1.0 到 1.2 | % |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.28 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.080 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 1830 | Mpa |
| -- 3 | 内部方法 | 1830 | Mpa | |
| -- 4 | ASTM D638 | 1810 | Mpa | |
| -- | ISO 527-2/1 | 1790 | Mpa | |
| Tensile Strength | Yield 5 | ASTM D638 | 47.0 | Mpa |
| Yield 6 | 内部方法 | 45.0 | Mpa | |
| Yield 7 | ASTM D638 | 44.0 | Mpa | |
| Yield | ISO 527-2/5 | 44.0 | Mpa | |
| Yield | ISO 527-2/50 | 47.0 | Mpa | |
| Break 7 | ASTM D638 | 50.0 | Mpa | |
| Break 6 | 内部方法 | 47.0 | Mpa | |
| Break 5 | ASTM D638 | 48.0 | Mpa | |
| Break | ISO 527-2/5, ISO 527-2/50 | 43.0 | Mpa | |
| Tensile Elongation | Yield 7 | ASTM D638 | 4.6 | % |
| Yield 6 | 内部方法 | 4.6 | % | |
| Yield 5 | ASTM D638 | 4.0 | % | |
| Yield | ISO 527-2/5 | 4.1 | % | |
| Yield | ISO 527-2/50 | 4.6 | % | |
| Break 7 | ASTM D638 | 120 | % | |
| Break 6 | 内部方法 | 110 | % | |
| Break 5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/5 | 110 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Flexural Modulus | 50.0 mm Span 8 | ASTM D790 | 1660 | Mpa |
| -- 9 | ISO 178 | 1860 | Mpa | |
| Flexural Stress | -- 9, 10 | ISO 178 | 71.0 | Mpa |
| Yield, 50.0 mm Span 8 | ASTM D790 | 70.0 | Mpa | |
| Break, 50.0 mm Span 8 | ASTM D790 | 69.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 108 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 117 | °C | |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Bf | 109 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 95.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Af | 87.0 | °C | |
| Vicat Softening Temperature | -- | ASTM D152513, ISO 306/B5013 | 119 | °C |
| -- | ISO 306/B120 | 122 | °C | |
| Coefficient of Linear Thermal Expansion | Flow : -40 to 95°C | ASTM E831 | 9.8E-5 | cm/cm/°C |
| Flow : -30 to 80°C | ISO 11359-2 | 9.8E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 1.0E-4 | cm/cm/°C | |
| Across Flow : -30 to 80°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 110 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Max Moisture | 0.020 | % | ||
| Suggested Shot Size | 50 到 80 | % | ||
| Rear Temperature | 245 到 265 | °C | ||
| Middle Temperature | 250 到 270 | °C | ||
| Front Temperature | 255 到 275 | °C | ||
| Nozzle Temperature | 255 到 270 | °C | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 65 到 90 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 50 到 80 | rpm | ||
| Vent Depth | 0.013 到 0.020 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 47 | kJ/m² |
| 23°C | ISO 179/1eA | 55 | kJ/m² | |
| Instrumented Dart Impact | -40°C, Energy at Peak | ASTM D3763 | 49.0 | J |
| -40°C, Total Energy | ASTM D3763 | 59.0 | J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 | J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 | J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 | J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 | J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 | J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.