Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 15 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 15 | g/10min |
Modeling Shrinkage | MD:3.20mm | ASTMD955 | 0.30to0.60 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/50 | 2400 | Mpa |
Tensile Strength | Yield | ASTMD638 | 44.0 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 45.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 48.0 | Mpa |
Tensile Elongation | Break | ASTMD638 | 25 | % |
Tensile Strain | Break | ISO527-2/50 | 10 | % |
Flexural Modulus | | ASTMD790 | 2500 | Mpa |
Flexural Modulus | | ISO178 | 2700 | Mpa |
Flexural Strength | | ASTMD790 | 74.0 | Mpa |
Flexural Stress | | ISO178 | 90.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 96.0 | °C |
Heat Deflection Temperature | 0.45MPa,Annealed,4.00mm | ISO75-2/B | 104 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 89.0 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 84.0 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed,4.00mm | ISO75-2/A | 101 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 102 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 104 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 16 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 11 | kJ/m² |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 113 | |
Rockwell Hardness | R-Scale | ISO2039-2 | 115 | |
Pencil Hardness | | JISK5401 | HB | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.0mm | UL94 | HB | |
Flame Rating | 1.5mm | UL94 | HB | |
Flame Rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.