Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 1.6 | g/10min |
| Melt Mass-Flow Rate | 210°C/2.16kg | ISO1133 | 3.8 | g/10min |
| EthyleneContent | | 内部方法 | 32.0 | mol% |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2 | 2700 | Mpa |
| Tensile Stress | Break | ISO527-2 | 34.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 15 | % |
| Flexural Modulus | | ISO178 | 3800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Peak Crystallization Temperature | | ISO11357-3 | 161 | °C |
| Glass Transition Temperature | | ISO11357-2 | 69.0 | °C |
| Vicat Softening Temperature | | ISO306 | 173 | °C |
| Melting Temperature | | ISO11357-3 | 183 | °C |
| Films Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Transmission Rate | 20°C,100%RH | ISO14663-2 | 0.38 | cm³·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 20°C,35%RH | ISO14663-2 | 6E-03 | cm³·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 20°C,65%RH | ISO14663-2 | 8E-03 | cm³·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 20°C,85%RH | ISO14663-2 | 0.030 | cm³·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 20°C,90%RH | ISO14663-2 | 0.060 | cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | | ASTME96 | 1.6 | g·mm/m²/atm/24hr |
| Oxygen Transmission Rate | 20°C,0%RH | ISO14663-2 | 4E-03 | cm³·mm/m²/atm/24hr |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | | ISO180 | 2.9 | kJ/m² |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.