PA9T Genestar™ G1302 BK KURARAY JAPAN

Unit Price:
$6004 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
56.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	320°C/2.16 kg	ASTM D1238	46	g/10 min
Modeling Shrinkage	Flow : 1.00 mm		0.20	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 1.00 mm		0.70	%
Moisture Absorption	Equilibrium, 40°C, 95%RH		1.4	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength		ASTM D638	165	Mpa
Tensile Elongation	Break	ASTM D638	4.0	%
Flexural Modulus		ASTM D790	9000	Mpa
Flexural Strength		ASTM D790	210	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load	1.8 MPa, Unannealed	ASTM D648	290	°C
Glass Transition Temperature			125	°C
Melting Temperature			306	°C

Electrical Properties	Test Condition	Test Method	Test Result	Unit
Volume Resistivity		ASTM D257	1.0E+16	ohms·cm
Dielectric Strength		ASTM D149	30	KV/mm
Dielectric Constant	10.0 GHz	ASTM D150	3.30
Dissipation Factor	10.0 GHz	ASTM D150	9.0E-3
Comparative Tracking Index		UL 746	PLC 0

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating		UL 94	HB
Bar Flow Length	320°C, 500.0 µm		5.50	CM
Weld Elongation		ASTM D638	0.70	%
Weld Strength		ASTM D638	47.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.