Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | 23°C | ISO 1183 | 1.18 | g/cm³ |
| Melt Volume flow Rate | 240°C/5.0 kg | ISO 1133 | 20.0 | cm3/10min |
| Modeling Shrinkage | Across Flow | ISO 2577 | 0.40 到 0.60 | % |
| Modeling Shrinkage | 流量 | ISO 2577 | 0.40 到 0.60 | % |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.40 | % |
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Tensile Stress | Yield, 23°C | ISO 527-2/50 | 64.0 | Mpa |
| Tensile Strain | Yield, 23°C | ISO 527-2/50 | 3.9 | % |
| Nominal Tensile Strain at Break | 23°C | ISO 527-2/50 | 40 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 95.0 | °C |
| Heat Deflection Temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 85.0 | °C |
| Vicat Softening Temperature | | ISO 306/B120 | 103 | °C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+16 | ohms |
| Volume Resistivity | 23°C | IEC 60093 | 1.0E+16 | ohms·cm |
| Relative Permittivity | 23°C, 100 Hz | IEC 60250 | 3.00 | |
| Relative Permittivity | 23°C, 1 MHz | IEC 60250 | 2.90 | |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 240°C | ISO 11443-A | 150 | Pa·s |
| ISO Shortname | | | PC+ABS-FR(40) | |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature () | | | 80 | °C |
| Dry Air Dryer | | | 4.0 | hr |
| Suggested Max Moisture | | | < 0.020 | % |
| Suggested Shot Size | | | 30 到 70 | % |
| Rear Temperature | | | 220 到 230 | °C |
| Middle Temperature | | | 225 到 235 | °C |
| Front Temperature | | | 230 到 240 | °C |
| Nozzle Temperature | | | 255 到 265 | °C |
| Processing (Melt) Temp | | | 240 到 270 | °C |
| Mold Temperature | | | 60 到 90 | °C |
| Back Pressure | | | 5.00 到 15.0 | Mpa |
| Vent Depth | | | 0.025 到 0.075 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ISO 180/A | 30 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.5 mm | UL 94 | V-0 | |
| Flame Rating | 2.0 mm | UL 94 | 5VB | |
| Oxygen Index | | ISO 4589-2 | 34 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.