PC Makrolon® 2805 COVESTRO GERMANY

226

Unit Price:
$2179 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 130****13

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density / Specific Gravity	23°C	ISO1183	1.20	g/cm³
Apparent Density		ISO60	0.66	g/cm³
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.00	cm3/10min
Modeling Shrinkage	TD	ISO2577	0.60to0.80	%
	Modeling Shrinkage	MD	ISO2577	0.60to0.80	%
		Modeling Shrinkage	TD:2.00mm3	ISO294-4	0.70	%
		Modeling Shrinkage	Modeling Shrinkage	MD:2.00mm3	ISO294-4	0.65	%
Moisture Absorption	Saturation,23°C	ISO62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.12	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	23°C	ISO527-2/1	2400	Mpa
Tensile Stress	Yield,23°C	ISO527-2/50	66.0	Mpa
Tensile Stress	Tensile Stress	Break,23°C	ISO527-2/50	70.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2/50	6.2	%
Tensile Strain	Tensile Strain	Break,23°C	ISO527-2/50	130	%
Nominal Tensile Strain at Break	23°C	ISO527-2/50	>50	%
Tensile Creep Modulus	1hr	ISO899-1	2200	Mpa
Tensile Creep Modulus	1000hr	ISO899-1	1900	Mpa
Flexural Modulus	23°C	ISO178	2400	Mpa
Flexural Stress	3.5%Strain,23°C	ISO178	73.0	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	97.0	Mpa
Flexural Strain	23°C	ISO178	7.1	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Linear Thermal Expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Thermal Conductivity	23°C	ISO8302	0.20	W/m/K
RTIElec	1.5mm	UL746	125	°C
RTIImp	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C
Heat Deflection Temperature	0.45MPa,Unannealed	ISO75-2/B	137	°C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,Unannealed	ISO75-2/A	125	°C
Glass Transition Temperature		ISO11357-2	145	°C
Vicat Softening Temperature	--	ISO306/B50	144	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	146	°C
Ball PressureTest	136°C	IEC60695-10-2	Pass
Coefficient of Linear Thermal Expansion	MD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C

Electrical Properties	Test Condition	Test Method	Test Result	Unit
Dissipation Factor	23°C,100Hz	IEC60250	5E-04
Dissipation Factor	Dissipation Factor	23°C,1MHz	IEC60250	9E-03
Comparative Tracking Index	SolutionA	IEC60112	250	V
Comparative Tracking Index	Comparative Tracking Index	SolutionB	IEC60112	125	V
Surface Resistivity		IEC60093	1E+16	ohms
Volume Resistivity	23°C	IEC60093	1E+16	ohms·cm
Dielectric Strength	23°C,1.00mm	IEC60243-1	34	KV/mm
Relative Permittivity	23°C,100Hz	IEC60250	3.10
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.00

Films Properties	Test Condition	Test Method	Test Result	Unit
Gas Permeation	Oxygen:23°C,100.0µm	ISO2556	650	cm³/m²/bar/24hr
WaterVaporTransmissionRate	23°C,85%RH,100µm	ISO15106-1	15	g/m²/24hr
Gas Permeation	CarbonDioxide:23°C,25.4µm	ISO2556	16900	cm³/m²/bar/24hr
	Gas Permeation	CarbonDioxide:23°C,100.0µm	ISO2556	3800	cm³/m²/bar/24hr
		Gas Permeation	Nitrogen:23°C,25.4µm	ISO2556	510	cm³/m²/bar/24hr
			Gas Permeation	Nitrogen:23°C,100.0µm	ISO2556	120	cm³/m²/bar/24hr
			Gas Permeation	Gas Permeation	Oxygen:23°C,25.4µm	ISO2556	2760	cm³/m²/bar/24hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C,Complete Break	ISO7391	16	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO7391	75	kJ/m²
Charpy Unnotched Impact Strength	-60°C	ISO179/1eU	NoBreak
	Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod Impact Strength	-30°C,Complete Break	ISO7391	15	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C,Partial Break	ISO7391	70	kJ/m²
Multi-Axial Instrumented Impact Energy	-30°C	ISO6603-2	65.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO6603-2	60.0	J
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO6603-2	6300	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO6603-2	5400	N

Hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	115	Mpa

Optical	Test Condition	Test Method	Test Result	Unit
Light Transmittance	4000µm	ISO13468-2	87.0	%
Haze	3000µm	ISO14782	<0.80	%
RefractiveIndex11		ISO489	1.586
Light Transmittance	1000µm	ISO13468-2	89.0	%
	Light Transmittance	2000µm	ISO13468-2	89.0	%
	Light Transmittance	Light Transmittance	3000µm	ISO13468-2	88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	900	°C
Oxygen Index		ISO4589-2	28	%
ApplicationofFlamefromSmallBurner-MethodKandF	2.00mm	DIN53438-1,-3	K1,F1
FMVSS Flammability	>1.00mm	ISO3795	passed
FlashIgnitionTemperature		ASTMD1929	480	°C
Glow Wire Test	1.50mm	EDFHN60E.02	750	°C
Glow Wire Test	Glow Wire Test	3.00mm	EDFHN60E.02	750	°C
Needle Flame Test	MethodF:1.50mm	IEC60695-11-5	1.0	min
Flame Rating	2.5mm	UL94	HB
Flame Rating	Flame Rating	0.75mm	UL94	V-2
Glow Wire Flammability Index	0.75mm	IEC60695-2-12	850	°C
	Glow Wire Flammability Index	1.5mm	IEC60695-2-12	850	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	930	°C
Glow Wire Ignition Temperature	0.75mm	IEC60695-2-13	875	°C
Needle Flame Test	MethodF:2.00mm	IEC60695-11-5	1.0	min
	Needle Flame Test	MethodF:3.00mm	IEC60695-11-5	2.0	min
		Needle Flame Test	MethodK:1.50mm	IEC60695-11-5	0.1	min
			Needle Flame Test	MethodK:2.00mm	IEC60695-11-5	0.1	min
			Needle Flame Test	Needle Flame Test	MethodK:3.00mm	IEC60695-11-5	0.2	min
SelfIgnitionTemperature		ASTMD1929	550	°C

Additional	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion	23°C	IEC60426	A1
ISO Shortname			ISO7391-PC,MR,(,,)-09-9

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.