POM Delrin® 100 NC010 DUPONT JAPAN
29
- Unit Price:
- $3728 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 94MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt Mass-Flow Rate | ISO1133 | 2.3 | g/10min | |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 1.90 | cm3/10min |
Modeling Shrinkage | TD | ISO294-4 | 1.8 | % |
MD | ISO294-4 | 2.2 | % | |
Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.90 | % |
Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
MeltDensity | 1.19 | g/cm³ | ||
SpecificHeatCapacityofMelt | 3000 | J/kg/°C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Modulus | ISO527-2 | 3000 | Mpa | |
Tensile Stress | Yield | ISO527-2 | 72.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 26 | % |
Nominal Tensile Strain at Break | ISO527-2 | 45 | % | |
Tensile Creep Modulus | 1hr | ISO899-1 | 2900 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 1600 | Mpa |
Flexural Modulus | ISO178 | 2900 | Mpa | |
Flexural Stress | 3.5%Strain | ISO178 | 79.0 | Mpa |
Compressive Stress | ISO604 | 110 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Coefficient of Linear Thermal Expansion | MD:-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
TD:-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
TD:-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
TD:AnnealingTemperature | ISO11359-2 | 160 | °C | |
TD:AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm | |
TD:EffectiveThermalDiffusivity | ISO11359-2 | 1E-07 | m²/s | |
Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
1.8MPa,Unannealed | ISO75-2/A | 100 | °C | |
Vicat Softening Temperature | -- | ISO306/A50 | 175 | °C |
-- | ISO306/B50 | 160 | °C | |
Melting Temperature | ISO11357-3 | 178 | °C | |
Coefficient of Linear Thermal Expansion | MD:-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Surface Resistivity | IEC60093 | 3E+13 | ohms | |
Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
Dielectric Strength | IEC60243-1 | 41 | KV/mm | |
Relative Permittivity | 100Hz | IEC60250 | 3.90 | |
1MHz | IEC60250 | 3.80 | ||
Dissipation Factor | 100Hz | IEC60250 | 1E-03 | |
1MHz | IEC60250 | 5.5E-03 | ||
Comparative Tracking Index | IEC60112 | 600 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 430 | kJ/m² |
23°C | ISO179/1eU | NoBreak |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | M-Sale | ISO2039-2 | 90 | |
R-Sale | ISO2039-2 | 121 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Burning Rate | 1.00mm | ISO3795 | 30 | mm/min |
Flame Rating | 0.8mm | UL94 | HB | |
1.5mm | UL94 | HB | ||
0.8mm | IEC60695-11-10,-20 | HB | ||
1.5mm | IEC60695-11-10,-20 | HB | ||
FMVSS Flammability | FMVSS302 | B | ||
Haze | F-value(refraction) | ISO6452 | 91 | % |
G-value(condensate) | ISO6452 | 1E-04 | g |
Additional | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Emission | VDA275 | <8.00 | mg/kg | |
EmissionofOrganicCompounds | VDA277 | 4.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.