PA66 AKROMID® A3 1 S3 AKRO-PLASTIC GERMANY

Unit Price:
$3923 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
28MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density	23°C	ISO1183	1.10	g/cm³
Spiral Flow		内部方法	80.0	CM
Modeling Shrinkage	TD	ISO294-4	2.2	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	2.1	%
HumidityAbsorption-	70°C	ISO1110	2.1	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ISO527-2/1	2700	Mpa
Tensile Stress	屈服	ISO527-2/50	63.0	Mpa
Flexural Stress		ISO178	90.0	Mpa
Flexural Strain (Break)		ISO178	7.5	%
Tensile Strain	断裂	ISO527-2/50	>35	%
Flexural Modulus		ISO178	2500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Heat Deflection Temperature	0.45MPa,未退火	ISO75-2/B	213	°C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO75-2/A	70.0	°C
Melting Temperature		DINEN11357-1	262	°C

Electrical Properties	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	1E+14	ohms
Volume Resistivity		IEC60093	1E+15	ohms·cm
Comparative Tracking Index	解决方案A	IEC60112	600	V

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-40°C	ISO180/1A	12	kJ/m²
	Notched Izod Impact Strength	-20°C	ISO180/1A	12	kJ/m²
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	15	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	17	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Burning Rate	1.00mm	FMVSS302	<100	mm/min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.